Organization and Performance of the Novel High Aluminum Zinc-Based Alloy

Abstract:

The novel high aluminum zinc-based alloy is prepared by changing composition of the alloy and adding 0.05% mixed rare earth with lanthanum-rich. The microstructure, mechanical properties and thermal expansion coefficient are investigated under as casting condition. The results showed that the novel high aluminum zinc-based alloy had fine microstructure, higher mechanical properties and smaller thermal expansion coefficient compared to the ZA27 alloy.

• Periodical: Advanced Materials Research (Volumes 750-752)
• Pages: 705-710
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.750-752.705
• Online since: August 2013
• Authors: Jia Ming Ji*, Hong Hong Shao, Guo Cui Meng, Dong Qing Gu
• Keywords: High Aluminum Zinc-Based Alloy, Mechanical Property, Microstructure, Mixed Rare Earth, Thermal Expansion Coefficient

References

[1] BU Jing-wei, Research status and prospects of cast zinc aluminum alloy ZA27 modification [J]. Journal Changzhou Institute of Technology, 2008(1): 1-2.

[2] LI Gui-ling, XIA Lan-ting, LIN Hong-bin. Effects of Al content on organization of high aluminum zinc-based alloy [J]. China Foundry Machinery & Technology, 2009(3): 22-24.

[3] TEMEL SAVA, ZEKI AZAKL. An investigation of lubricated friction and wear properties of Zn-40Al-2Cu-2Si alloy in comparison with SAE65 bearing bronze [J]. Wear, 2008, 264: 920-928.

DOI: 10.1016/j.wear.2007.06.008

[4] YAN Cheng-jun, WANG Ji-dai, SUN Jing. Effects of rare-earth oxides on the mechanical properties of high aluminum zinc-based alloy [J]. Foundry Technology, 2006(8): 842-844.

[5] CHENG Xin, SONG Dong-ming, WANG Yun-kun. Research of the casting process of high aluminum zinc-based hot-dip alloy [J]. Yunnan Metallurgy, 2009(3): 40-42.

[6] PRASAD B K, PATWARDHAN A K, YEGNESWARNAN AH. Microstructure property characterization of some ZnAl alloy: effect of heat treatment parameters[J]. Z. Metallked, 1996, 87(12): 967-971.

DOI: 10.1515/ijmr-1996-871206

[7] LI An-ming, NAN Hong-yan, DAI Yong-juan. Effects of Si, Al and rare earth on microstructures and properties of casting zinc-based alloys[J]. Foundry, 2002, 51(11): 695-697.

[8] YANG Di-xin, GAO Cun-zhen, XIE Jing-pei. Effects of Cu content on the microstructures and properties of high aluminum zinc alloy [J]. Foundry Technology, 2010, 31(11): 1448-1451, 41-43.

[9] Chen Mei-ling, Chen Yu-xi. Researches of thermal expansion properties of high aluminum zinc-based alloy [J]. Special Casting & Nonferrous Alloys, 1999, (1): 5 -6.

[10] FENG Jian-qing, Zeng Jian-min, ZOU Yong-zhi. Researches of mechanical properties and microstructures of high aluminum zinc -based alloy [J]. Materials for Mechanical Engineering, 2004, 28(11).

[11] YAN Shu-qing, XIE Jing-pei. Effects of cooling rate and Al content on microstructures and hardness of zinc alloy [J]. Hot Working Technology, 2007 (16): 10-12.

[12] XU Chun-xiang, Zhao Pei-lian. Effects of mixed rare earth on mechanical properties of ZA27 alloy at high temperature [J]. Materials Science and Technology, 1999, 7(3): 105 -108.

[13] MU Dong, WEI Xiao-Wei. Research status of microstructure and properties of ZA27 alloy with RE[J]. Sichuan Institute of Technology, 2004, 23 Suppl (3): 238 -240.

[14] XIANG Liu-shuan. New method of [J]. Materials Review, 1994, (3): 13-16.