The Corrosion Behavior of 07/09Cr2AlMoRE Used for Petro-Chemical Equipment

Abstract:

The stress corrosion property of 07/09Cr2AlMoRE and its welding joint were investigated under different conditions. The results showed that the anti-SSC performance of welding joint was lower than that of the plate through the Sc experiment. The martensite and overheated structure appeared owing to the improper control during welding and heat treatment, which resulted in the lower anti-SSC property of welding joint. The temperature and Ph value had important effect on corrosion rate through analysis the data of comprehensive corrosion. The corrosion rate would rise 1 times when the temperature increased 30°C. The corrosion rate was improved nearly by one order of magnitude when the pH value decreased from 6 to 4. The corrosion surface was uniform and no any corrosion pit, which indicated that the microstructure and chemical component was nearly uniform.

• Periodical: Advanced Materials Research (Volumes 750-752)
• Pages: 765-770
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.750-752.765
• Online since: August 2013
• Authors: Yu Fu Zhang, Ying Ma, Yuan Hao, Hui Xia Guo, Wen Ming Song
• Keywords: Complicated Condition, Comprehensive Corrosion, Pressure Vessel, Stress Corrosion

References

[1] ZHANG Bao-hong, CONG Wen-bo, YANG Ping. Metal electrochemical corrosion and protection, Chemical Industry Press, Beijing, 2005. 134-138.

[2] WANG Ke, ZHENG Zhen-tai, DONG Tian-shun. Welding technology, 2012, 41(4): 4-9.

[3] JB/T 4730. 3—2005, Nondestructive Testing of Pressure Equipments, 3 rd. part: Ultrasonic Testing[S].

[4] JB/T 4730. 4—2005, Nondestructive Testing of Pressure Equipments, 4 th. Part: Magnetic particle testing [S].

[5] JB/T 4730. 2-2005, Nondestructive Testing of Pressure Equipments, 2 nd. Part: The X-ray testing [S].

[6] ASTM G1-03, Standard Practice for Preparing, Cleaning, and Evaluating Corrosion Test Specimens [S].

[7] JB/T 10579 -2006, Standard method for corrosion data statistical analysis[S].

[8] GB/T 8170-2008, Rules for rounding off of numerical values & present and judgment of the limit values [S].

[9] NACE TM0177-2005, Laboratory Testing of Metals for Resistance to Sulfide Stress Cracking and Stress Corrosion Cracking in H2S Environments[S].

[10] JB/T 7901-1999, Full immersion uniform corrosion test method in laboratory for metal materials[S].

[11] ASTM G31 - 72(2004) Standard Practice for Laboratory Immersion Corrosion Testing of Metals[S].

[12] Schmitt G. Fundamental aspects of CO2 corrosion. In: Hausler R H, Giddard H P(Eds), Advances in CO2 corrosion. NACE, Houston, Texas, 1984(1. 1): 10.