Microstructure and Properties of Alloys with Equal Atomic Principal Components

Abstract:

Four high-entropy alloys are prepared by an arc furnace under argon atmosphere. The microstructure and the properties of the alloys are investigated. The results show that NiCrCuCoFe alloy consists of a single FCC solid solution. When Al presents in the alloys, the microstructures of the alloys change to a BCC+ FCC solid solution. It is indicated that Al element promotes the formation of BCC solid solution, and Si and Mn promote the formation of complicated compounds. The hardness of alloys with BCC structure is higher than that of the alloys with FCC structure. The complicated compounds are formed, the hardness increases further. The highest hardness of the alloys reaches 882 HV due to the strengthening of the second phase precipitation.

• Periodical: Advanced Materials Research (Volumes 765-767)
• Pages: 3143-3146
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.765-767.3143
• Online since: September 2013
• Authors: Yan Ping Wang, Yu Zhuang, Jian Chen Li
• Keywords: High-Entropy Alloy, Microstructure, Property

References

[1] J. W. Yeh, S. K. Chen, S. J. Lin, J. Y. Gan, T. S. Chin, T. T. Shun, C. H. Tsau, S.Y. Chang: Adv. Eng. Mater., Vol. 6 (2004), p.299.

[2] J. W. Yeh, S. K. Chen, J. Y. Gan, S. J. Lin, T. S. Chin, T. T. Shun, C. H. Tsau, S. Y. Chang: Metall. Mater. Trans. A Vol. 35 (2004), p.2533.

[3] P. K. Huang, J. W. Yeh, T. T. Shun, S. K. Chen: Adv. Eng. Mater. Vol. 6, (2004), p.74.

[4] C. Y. Hsu, J. W. Yeh, S. K. Chen, T. T. Shun: Metall. Mater. Trans. A Vol. 35, (2004), p.1465.

[5] Y. Y. Chen, T. Duval, U. D. Hung, J. W. Yeh, H. C. Shih: Corros. Sci. Vol. 47 (2005), p.2257.

[6] Y. S. Huang, L. Chen, H. W. Lui, M. H. Cai, J. W. Yeh: Mater. Sci. Eng. A Vol. 457 (2007), p.77.

[7] C. C. Tung, J. W. Yeh, T. T. Shun, S. K. Chen, Y. S. Huang: Mater. Lett., Vol. 61, (2007), p.1.

[8] S. W. Kao, J. W. Yeh, T. S. Chin: J. Phys. C Vol. 20 (2008), p.145214.

[9] Y. J. Zhou, Y. Zhang, T. N. Kim, G. L. Chen: Mater. Lett. Vol. 62 (2008), p.2673.

[10] S. Varalakshmi, M. Kamaraj, B. S. Murty: J. Alloys Compounds Vol. 460 (2008), p.253.

[11] H. W. Chang, P. K. Huang, J. W. Yeh, A. Davison, C. H. Tsau, C. C. Yang: Surf. Coating Technol. Vol. 202 (2008), p.3360.

[12] B. Cantor, I. T. H. Chang, P. Knight, A. J. B. Vincent: Mater. Sci. Eng. A Vol. 375-377 (2004), p.213.

[13] C. Li, J. C. Li, M. Zhao, L. Zhang, Q. Jiang: Mater. Sci. Technol. Vol. 24 (2008), p.376.

[14] Y. J. Zhou, Y. Zhang, Y. L. Wang, G. L. Chen: Appl. Phys. Lett. Vol. 90 (2007), p.181904.

[15] M. Chen, Y. Liu, Y. X. Li: Acta Meall. Sinica. Vol. 43 (2007), p.1020.

[16] U. S. Hsu, U. D. Hung, J. W. Yeh, S. K. Chen, Y. S. Huang, C. C. Yang: Mater. Sci. Eng. A Vol. 469 (2007), p.403.

[17] Y. J. Zhou, Y. Zhang, Y. L. Wang, G. L. Chen: Mater. Sci. Eng. A Vol. 454 (2007), p.260.

[18] Y. Zhang, Y. J. Zhou, J. P. Lin, G. L. Chen, P. K. Liaw: Adv. Eng. Mater. Vol. 10 (2008), p.534.