Considerations on the Micro-Indentation and Differential Scanning Calorimetry of Arboform Reinforced with Aramid Fibres

Article Preview

Abstract:

The researches made in the last years have shown that lignin is a substance that gives wood strength. It can be found in the granular form that can be melted and injected. Lignin is used to obtain material with multiple uses such as electronics, food containers etc. This material is known as "liquid wood". Fibers with high specific resistance and high elasticity modules, such as aramid fibers, are used to create high performance composites. Here are the main physical-mechanical properties of aramid fibers: high tensile strength, high shock resistance, high stresses and fatigue, excellent characteristics of damping vibrations, exposure characteristics preservation at temperatures ranging from-700C to + 1800C, flame resistance (self-extinguishing, not melting), low smoke emission, corrosion stability, good electrical characteristics, low conductivity and low dielectric constant. The main areas of use of aramid wires are: special clothes resistance to cutting and high temperature components for materials composite, ropes, cables, lashing straps, safety equipment for the armed forces, police, aircraft, etc. This research used Arboform L, V3 Nature reinforced with aramid fiber. The experimental research plan observes the Taguchi methodology with 6 input factors, each with two levels of variation. The input parameters effects are analyzed on the mechanical properties of the specimens obtained. Micro-indentation tests and differential scanning calorimetry were conducted. The studied test samples showed the following mean recovery values: 31.219μm for the first sample, 31.059μm for the second sample and 25.996μm for the third sample. Three extreme points were detected on the DSC thermogram: an endothermic peak occurs up to 380 K (I) and an exothermic one of higher intensity (II); above 430 K the DSC thermogram shows a deviation from linearity of the flow heat, which suggests a melting phenomenon. The first variation of the heat flow can be attributed to the transformations that occur in solid form in the sample subjected to heating, the first adsorption heat exchanger (peak I) and the second heat releasing (peak II). Comparing the amount of heat absorbed by heat dissipation, one may notice that the exothermic conversion is increased. The initial transformation temperature (Ts 10) corresponds to 10% of the total peak area while the final transformation temperature (Tf 90) corresponds to 90% of the total surface area.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

718-723

Citation:

Online since:

November 2013

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2014 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] C. Schick , Calorimetry, Polymer Science: A Comprehensive Reference, 2, (2012), p.793–823.

Google Scholar

[2] P. Zhou, T.P. Labuza, Analytical Methods /Differential Scanning Calorimetry, Encyclopedia of Dairy Sciences (Second Edition), (2011), p.256–263.

DOI: 10.1016/b978-0-12-374407-4.00026-1

Google Scholar

[3] A. V. Svanidze, H. Huth, S. G. Lushnikov, C. Schick, Study of phase transition in tetragonal lysozyme crystals by AC-nanocalorimetry, Thermochimica Acta 544 (2012) p.33– 37.

DOI: 10.1016/j.tca.2012.06.013

Google Scholar

[4] M. Benke, F. Tranta, P. Barkoczy, V. Mertingera, L. Daroczi, Effects of heat-flux features on the differential scanning calorimetry curve of a thermoelastic martensitic transformation, Materials Science and Engineering A 481–482 (2008) p.522–525.

DOI: 10.1016/j.msea.2007.01.184

Google Scholar

[5] N. M. Lohan, B. Pricop, L. G. Bujoreanu, N. Cimpoeşu, Heating rate effects on reverse martensitic transformation in a Cu-Zn-Al shape memory Alloy, International Journal of Materials Research – 102, 11 (2011), pp.1345-1351.

DOI: 10.3139/146.110595

Google Scholar

[6] S. Montserrat, Y. Calventus, J.M. Hutchinson, Effect of cooling rate and frequency on the calorimetric measurement of the glass transition, Polymer, 46, 26, (2005), p.12181–12189.

DOI: 10.1016/j.polymer.2005.10.138

Google Scholar

[7] T. Kousksou, A. Jamil, K. El Omari, Y. Zeraouli, Y. Le Guer, Effect of heating rate and sample geometry on the apparent specific heat capacity: DSC applications, Thermochimica Acta, 519, 1–2, (2011), p.59–64.

DOI: 10.1016/j.tca.2011.02.033

Google Scholar

[8] N. M. Lohan, L. -G. Bujoreanu, C. Baciu, Influence of temperature variation rate on calorimetric response during heating and on martensite structure obtained after subsequent cooling of Cu–Zn–Al shape memory alloy, Micro & Nano Letters, 7, 6, (2012).

DOI: 10.1049/mnl.2012.0049

Google Scholar

[9] Ciofu, C, Mindru, T.D., Injection and micro injection of polymeric plastics materials: A review, International Journal of Modern Manufacturing Technologies, Vol. V, No. 1/2013, pp.49-68.

Google Scholar

[10] D. Nedelcu, O. Pruteanu, Aspecte ale formarii canelurilor exterioare prin deformare plastic la rece utilizand metoda Taguchi, Tehnica-Info Publishing House, pp.243-261, Chisinau, (2000).

Google Scholar

[11] Seres, I., Injectarea materialelor plastice, Imprimeria de Vest Publishing House, pp.314-325, Oradea, (1996).

Google Scholar

[12] Płaczek M.: Indication of the suitable model of a mechatronic system as an introduction to the synthesis task, Journal of Achievements in Materials and Manufacturing Engineering, JAMME, vol. 49/2, pp.338-349, December (2011).

Google Scholar

[13] http: /www. revistamagazin. ro/content/view/6838/20/, Accessed: 16. 06. (2013).

Google Scholar

[14] http: /www. casamea. ro/casa/constructii/materiale/lemnul-lichid-6542, Accessed: 15. 06. (2013).

Google Scholar