Crack Growth Study of Dissimilar Steels (Stainless - Structural) Butt and Overlap Welded Unions under Cyclic Load

Abstract:

This study describes the mechanisms of emergence and propagation of fatigue cracks caused by mechanical tension stress fluctuations in dissimilar steels butt and overlap welded joints under axial tension fatigue loads. A structural (ASTM A537, class I) and a stainless (ASTM A240, 304L) were soldiers through GMAW, Argon as protecting gas and a stainless (ASTM A240, 308L) as a supplier material, not being submitted to pre and post welding thermal treatment. Microstructures (Scanning Electron Microscopy, SEM) were contrasted in different zones of each joint, focus on Heat Affected Zone (HAZ) and fusion lines. Samples were inspected by not destructive test (penetrating liquids and ultrasound), to discard surface and internal defects. The following mechanical tests were compared between both welding joint (WJ): Vickers hardness profile, tension, bending, impact, axial fatigue, and speed of propagation of fatigue cracks. Vickers show high values of micro hardness in the HAZ, near the fusion line between weld and stainless. Tension and axial fatigue tests indicated similar behavior between WJ and structural (butt joint); and similar behavior between WJ and stainless (overlap joint). Pre-cracked test evidence a faster growth of crack in the fusion line between structural steel and stainless. Dissimilar unions (butt and overlap) have mechanical and microstructure properties, which can be considered adequate to withstand the mechanical requirements in service conditions, despite relatively high values of hardness in the HAZ, particularly in the fusion line between the welding cord and the stainless 304L, as well as inclusions between the structural and the stainless one.

• Periodical: Advanced Materials Research (Volumes 891-892)
• Pages: 1645-1650
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.891-892.1645
• Online since: March 2014
• Authors: Andrés L. García Fuentes*, Alberto Velásquez del Rosario
• Keywords: Axial Fatigue, Crack Growth, Dissimilar Welding, Stainless Steel (SS)

References

[1] Garcia, A, Centeno, L, Salas, R, y Velazquez, A, Metallurgy of dissimilar steels welded unions (ASTM A240–A537) and mechanical behavior under monotonic and cyclic loads. Latin American Journal of Metallurgy and Materials, pISSN: 0255-6952 | eISSN: 2244-7113. 24 May (2011).

[2] Garcia, A, Centeno, L, Bazán, P, y Velazquez, A, Mechanical behavior of overlap-welded of dissimilar steels (structural-stainless) under monotonic load,. Advanced Materials Research. Advanced Materials and Processes II. Vols. 557-559. Publicado on-line: 20/07/2012. Vols. 557-559 (2012).

DOI: 10.4028/www.scientific.net/amr.557-559.1268

[3] ASTM A240/A240M (01). Standard Specification for Heat-Resisting Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels.

DOI: 10.1520/a0167-99r09

[4] ASTM A537/A537M-95 (2000). Standard Specification for Pressure Vessel Plates, Heat-Treated, Carbon-Manganese-Silicon Steel.

DOI: 10.1520/a0537_a0537m

[5] ANSI/AWS A5. 9/A5. 9M-2006: Corrosion - Resisting Chromium and Chromium - Nickel Steel Bare and Composite Metal Cored and Stranded Welding Electrodes and Welding Rods. Miami (EE. UU. ): American Welding Society, (2006).

DOI: 10.1520/a0371

[6] ASME CODE. Section IX. Welding and Brazing Qualifications (American Society of Mechanical Engineers). (2007).

[7] Welding handbook, Vol 1. AWS Handbook (American Welding Society), Eighth Edition. (2007).

[8] ASTM E3-01 Standard Practice for Preparation of Metallographic Specimens. Philadelphia (EE. UU. ): American Society for Testing and Materials, (2001).

[9] ASTM E92-82 (1997) e3 Standard Test Method for Vickers Hardness of Metallic Materials. Philadelphia (EE. UU. ): American Society for Testing and Materials, (1997).

[10] ASTM E8M-01 Standard Test Methods for Tension Testing of Metallic Materials [M]. Philadelphia (EE. UU. ): American Society for Testing and Materials, 01.

[11] Sindo, K, Welding Metallurgy. Department of Materials Science and Engineering University of Wisconsin (EE. UU. ): John Wiley & Sons, INC, Publication, 2002, Second Edition.

[12] GARCIA, A. Physical metallurgy of dissimilar steels (ASTM A240-A537) welded unions and mechanical behavior under monotonic and cyclic loads. 10th International Fatigue Congress, Institute of Physics of Materials of the Academy of Sciences, Czech Republic. Prague. (2010).

[13] GARCIA, A. Crack growth study of dissimilar steels (Stainless - Structural) butt welded unions under cyclic loads. Procedia Engineering 10 (2011) 1917–1923. ICM11.

DOI: 10.1016/j.proeng.2011.04.318