Characteristics of Bacterial Cellulose Production from Agricultural Wastes

Abstract:

There are increasing demands to substitute the plastic from the petrochemical industry with bacterial cellulose which were produced from microorganisms as Acetobactor xylinum strain. The aim of this study was to produce bacterial cellulose from banana peels which are agricultural waste around Walailak University area. The banana peels were used as a carbon source together with nutrient medium for the growth of bacteria. The ratio between Hestrin and Schramm nutrient medium (HS) with banana peel to DI water was 1:0.5, 1:1, and 1:1.5 (%V/V). Sugar content in banana peel (control) was 4.0% Degree Brix. The initial pH was 6.0 and sugar contents varied in this study were 5.5%, and 11% Degree Brix. A.xylinum dosages used in the cultivation were 5, 6.67, and 8.33 (%V/V) respectively. The cultivation times were 15 days at the temperature of 30 °C. As a result, the highest yield of produced bacterial cellulose was 19.46 gram and the best condition which maximum yield of bacterial cellulose 1.95% can be obtained was 11% (Brix) of sugar content, 6.67 (%V/V) of A.xylinum added, and 1:1.5 of banana peel to DI water. The physical properties of bacterial cellulose were studied with ATR-FTIR spectroscopy which shown adsorption spectrum at 3279, 2915, 1627 and 1013 cm^-1 corresponding to the-OH,-CH,-CH₂ and carboxyl function groups, respectively. Glass transition Temperature (T_g) was 116.85°C. Tensile strength was measured with UTM and had average value of 41.13±5.43 Mpa. The bacterial cellulose had moisture content of 90.00±0.02%. The synthesized bacterial cellulose can be used as adsorption media and also has its chemical properties like petroleum polymer. Result suggested that the similar property can be observed when compared with petroleum plastic, however with the exception of methyl group (CH₃). Methyl group which can be found in plastic synthesized from petrochemical is responsible for the strength of plastic. Thus, bacterial cellulose, synthesized in this study, is not as strong as petrochemical plastic. But it can be used to produce bio-plastics because of the-CH and-CH₂ functional group attached. With the similar physical and chemical properties to those of petrochemical plastic, bacterial cellulose can be used as biopolymer.

• Periodical: Advanced Materials Research (Volumes 931-932)
• Pages: 693-697
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.931-932.693
• Online since: May 2014
• Authors: Sunun Khami, Wipawee Khamwichit*, Kowit Suwannahong, Wipada Sanongraj
• Keywords: Acetobacter xylinum, Agricultural Waste, Bacterial Cellulose, Banana Peels

References

[1] Silviya Elanthikkal, Unnikrishnan Gopalakrishnapanicker, Soney Varghese, James T Guthrie. Cellulose microfibres produced from banana plant wastes: Isolation and characterization. Carbohydrate Polymers. 80 (2010) 852–859.

DOI: 10.1016/j.carbpol.2009.12.043

[2] Xiaobo Zeng, Darcy P. Small, Wankei Wan. Statistical optimization of culture conditions for bacterial cellulose production by Acetobacter xylinum BPR 2001 from maple syrup. Carbohydrate Polymers. 85 (2011) 506–513.

DOI: 10.1016/j.carbpol.2011.02.034

[3] E. J. Vandamme., S. De Baets., A. Vanbaelen., K. Joris., and P. De Wulf. Improved production of bacterial cellulose and its application potential. polymer Degradation and Stability 59 (1998) 93-99.

DOI: 10.1016/s0141-3910(97)00185-7

[4] Ratthapol Rangkupan, Darrell H. Reneker. Electrospinning process of molten polypropylene in vacuum. Metals Materails and Minerals. 12 (2003) 81-87.

[5] Suwannahong. K., W. Liengcharoensit., W. Sanongraj., and J. Kruenate. Application of Nano-TiO2/LDPE Composite film on photocatalytic oxidation degradation of dichloromethane. Journal of Environmental. 33 (2012) 955-959.

[6] K.A. Khan., P. Musikabhumma., and J.P. Warr. The Effect of Moisture Content of Microcrystalline Cellulose on the Compressional Properties of Some Formulations. 7 (1981) 525-538.

DOI: 10.3109/03639048109057729

[7] T. Volkmer., L. Arietano., C. Plummer., J. Strautmann,. M. Noel. Loss of tensile strength in cellulose tissue on the surface of spruce (Picea abies) caused by natural photodegradation and delignification. Polymer Degradation and Stability. 98 (2013).

DOI: 10.1016/j.polymdegradstab.2013.03.019

[8] M Akerholm., B Hinterstoisser., and L Salmen. Characterization of the crystalline structure of cellulose using static and dynamic FT-IR spectroscopy. Carbohydrate Research. 3 (2004) 569-578.

DOI: 10.1016/j.carres.2003.11.012

[9] Dekui Shen., Jiangming Ye., Rui Xiao., and Huiyan Zhang. TG-MS analysis for thermal decomposition of cellulose under different atmospheres. Carbohydrate Polymers. 98 (2013) 514-521.

DOI: 10.1016/j.carbpol.2013.06.031