Microstructural Effect on the Rehealing Ability of Sputtered K38G Nanocrystalline Coating

Abstract:

Article Preview

Info:

Edited by:

A.R. Yavari, A. Inoue, D. Morris and R. Schulz

Pages:

1-8

Citation:

G. F. Chen and L. C. Zhang, "Microstructural Effect on the Rehealing Ability of Sputtered K38G Nanocrystalline Coating", Journal of Metastable and Nanocrystalline Materials, Vol. 12, pp. 1-8, 2002

Online since:

August 2002

Export:

Price:

$38.00

[1] H. Lou, F. Wang, S. Zhu, B. Xia, L. Zhang: Surf. Coat. Technol. Vol. 63 (1994), p.105.

[2] H. Lou, Y. Tang, X. Sun, H. Guan: Mater. Sci. Eng. Vol. A207 (1996), p.121.

[3] J. Zhang, H. Lou: Acta Metall. Sinica Vol. 34 (1998), p.627.

[4] G. Chen, H. Lou: Scripta Mater. Vol. 43 (2000), p.119.

[5] F. Wang: Oxid. Met. Vol. 48 (1997), p.215.

[6] Z. Liu, W. Gao, K. Dahm, F. Wang: Scripta Mater. Vol. 37 (1997), p.1551.

[7] F.H. Stott, G.C. Wood, J. Stringer: Oxid. Met. Vol. 44 (1995), p.113.

[8] G. Chen, H. Lou: Oxid. Met. Vol. 53 (2000), p.467.

[9] G. Chen, H. Lou: J. Mater. Sci. Lett. Vol. 19 (2000), p.1789.

[10] H. Lou, S. Zhu, F. Wang: Oxid. Met. Vol. 43 (1995), p.317.

[11] J. Zhang, H. Lou: Chinese. J. Nonferrous. Met. Vol. 8 suppl. 1 (1998), p.30.

[12] S.W. Yang: Oxid. Met. Vol. 15 (1981), p.375.

[13] G. Chen, H. Lou: Corros. Sci. Vol. 42 (2000), p.1185.

[14] J. Litz, A. Rahmel, M. Schorr: Oxid. Met. Vol. 30 (1988), p.95.

[15] T.R. Malow, C.C. Koch: Acta Mater. Vol. 45 (1997), p.2177.

[16] J. Zhang, Master Thesis, Institute of Corrosion and Protection of Metals, Academia Sinica, 1997 Figure captions: Fig. 1 XRD patterns of (a) the as-sputtered and (b) pre-oxidized K38G coating Fig. 2 (A) Bright-field micrograph and (B) corresponding SAD pattern of TiO2 and Al2O3 Fig. 1 XRD patterns of (a) the as-sputtered and (b) pre-oxidized K38G coating 20 30 40 50 60 70 80 TiC TiC TiC γ γγ b a Angle (2θ) Fig. 2 (A) Bright-field micrograph and (B) corresponding SAD pattern of TiO2 and Al2O3.

DOI: https://doi.org/10.7717/peerj.1277/supp-1

Fetching data from Crossref.
This may take some time to load.