Investigation of the Effect of Novel Two-Step Austenitization Process on the Microstructure and Mechanical Properties of ADI

Abstract:

A novel two step austenitization heat treatment process was conceived to develop ADI with optimum combination of strength, ductility and fracture toughness. This novel heat treatment process involved austenitizing the ductile iron in the lower intercritical temperature range and then raising the temperature to the fully austenitic temperature range followed by austempering in the bainitic temperature range. The resulting microstructure consisted of very fine scale bainitic ferrite, high-carbon austenite and pro-eutectoid ferrite. The proeutectoid ferrite is nucleated because of prior austenitization in the intercritical range which resulted in ADI with high fracture toughness without significantly compromising the strength and ductility. An analytical theory has been developed based upon the nucleation of proeutectoid ferrite and graphite nodules during intercritical austenitization, to explain this physical outcome.

• Periodical: Key Engineering Materials (Volume 1011)
• Pages: 11-17
• DOI: https://doi.org/10.4028/p-Dhr71i
• Online since: May 2025
• Authors: Deepak Joshi, Susil Putatunda*, Saranya Panneerselvam, James Boileau
• Keywords: Austempering, Intercritical, Microstructure, Phase Transformation, Two-Step Austenitization

References

[1] Cast Metals Development Ltd, Alvechurch, Birmi . "Austempered ductile-iron castings - advantages, production, properties and specifications", Materials & Design, 13, 5, 1992, 285-297.

DOI: 10.1016/0261-3069(92)90191-j

[2] K.B Rundman, K.L. Hayrynen, W.J. Dubensky & T.N. Rouns, "The Microstructure and Mechanical Properties of Austempered Ductile Iron", Journal of Heat Treating, 5(2),1988, 79-85.

DOI: 10.1007/bf02833175

[3] J.R. Keough, "Ductile Iron Data for Design Engineers – Section IV: Austempered Ductile Iron", Ductile Iron Society.

DOI: 10.1520/a0897-90r97

[4] R.C Voigt, "Austempered Ductile Iron—Processing and Properties", Cast Metals, Vol. 2 no. 2, 1988,71-93.

DOI: 10.1080/09534962.1989.11818986

[5] S.C. Murcia, M.A. Paniagua, E.A. Ossa, Development of as-cast dual matrix structure (DMS) ductile iron, Materials Science and Engineering: A, Volume 566,2013, pp.8-15.

DOI: 10.1016/j.msea.2012.12.033

[6] ASTM-E8, Standard test methods for tension testing of metallic materials. West Conshohocken, USA,2013.

[7] ASTM E-399, Standard Test Method for Plain Strain Fracture Toughness Testing of Metallic Materials, Annual Book of ASTM standard,P,3.01,1992, pp.745-756.

DOI: 10.1520/jte10604j

[8] K.L. Hayrynen, J.R. Keough and B.V. Kovacs," The Effects of Alloying Elements on the Critical Temperatures in Ductile Iron", Ductile Iron Society, Research Report No. 22, December 1997.

[9] B.D. Cullity Elements of X-ray diffraction. MA, USA,1974.

[10] C.S. Roberts," Effect of carbon on the volume fractions and lattice parameters of retained austenite and martensite." Journal of Metals., 1953,203-4.

DOI: 10.1007/bf03397477

[11] M.Erdogan, V.Kilicli & B. Demir ,"Transformation characteristic of Ductile Iron austempered from intercritical austenitization temperature range.", Journal of Material Science, 44, 2009, 1394-1404.

DOI: 10.1007/s10853-006-1415-7

[12] Reed-Hill RE. Physical metallurgy principles (4th edn).

[13] S.Panneerselvam ,C.J. Martis ,S.K Putatunda ,J.M. Boileau," An investigation on the stability of austenite in Austempered Ductile Cast Iron (ADI)." Materials Science and Engineering a-Structural Materials Properties Microstructure and Processing 626:2006, pp.237-246.

DOI: 10.1016/j.msea.2014.12.038

[14] J.H. Yang, S.K. Putatunda "Improvement in strength and toughness of austempered ductile cast iron by a novel two-step austempering process." Materials & Design 25(3): 2004, 219-230.

DOI: 10.1016/j.matdes.2003.09.021

[15] P.P. Rao ,S.K. Putatunda," Dependence of fracture toughness of austempered ductile iron on austempering temperature." Metallurgical and Materials Transactions a-Physical Metallurgy and Materials Science 29(12): 1998, 3005-3016.

DOI: 10.1007/s11661-998-0208-9