Effect of Contact Shape on the Cracking Behaviour
p.743

Study of Fracture Origin on Low Cycle Fatigue of Spheroidal Graphite Cast Iron Having Various Matrixes
p.749

The Propagation Behavior of Love Waves in a Pre-stressed Piezoelectric Layered Structure
p.755

The Effect of Nucleation Time on the Growth of a Microvoid in a Viscoelastic Material
p.761

Effects of Stress Fields around Micro-Surface Defects on the Occurrence of Slip and Micro Cracks
p.767

HomeKey Engineering MaterialsKey Engineering Materials Vols. 183-187Effect of Contact Shape on the Cracking Behaviour

Effect of Contact Shape on the Cracking Behaviour

Article Preview

Abstract:

You might also be interested in these eBooks

Fracture and Strength of Solids IV

Info:

Periodical:

Key Engineering Materials (Volumes 183-187)

Pages:

743-748

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.183-187.743

Citation:

Cite this paper

Online since:

April 2000

Authors:

Hyung Kyu Kim, Heung Seok Kang

Keywords:

Contact Failure, Crack Closure, Crack Opening Period, Edge Cracks, Fretting, Partial Slip, Punch Shape, Stress Intensity Factor (SIF)

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 2000 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation: