Study of Fracture Origin on Low Cycle Fatigue of Spheroidal Graphite Cast Iron Having Various Matrixes
p.749

The Propagation Behavior of Love Waves in a Pre-stressed Piezoelectric Layered Structure
p.755

The Effect of Nucleation Time on the Growth of a Microvoid in a Viscoelastic Material
p.761

Effects of Stress Fields around Micro-Surface Defects on the Occurrence of Slip and Micro Cracks
p.767

Studies of Fracture of Piezoelectric Ceramics at HKUST
p.773

HomeKey Engineering MaterialsKey Engineering Materials Vols. 183-187Study of Fracture Origin on Low Cycle Fatigue of...

Study of Fracture Origin on Low Cycle Fatigue of Spheroidal Graphite Cast Iron Having Various Matrixes

Article Preview

Abstract:

You might also be interested in these eBooks

Fracture and Strength of Solids IV

Info:

Periodical:

Key Engineering Materials (Volumes 183-187)

Pages:

749-754

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.183-187.749

Citation:

Cite this paper

Online since:

April 2000

Authors:

Kazuhiro Morino, Fumihito Nishimura, Hironobu Nisitani

Keywords:

Blind Hole, Cylindrical Specimen, Fatigue, Fracture Origins, Low Cycle Fatigue, Microshrinkage, Scanning Electron Microscope (SEM), Spheroidal Graphite Cast Iron

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 2000 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation: