Paper Titles

Thermal Aging and Low Cycle Fatigue Characteristics of CF8M in a Nuclear Reactor Coolant System
p.975

Study of Crack Propagation Behavior on Low Cycle Fatigue in Spheroidal Grahite Cast Iron Based on Observation of Surface and Fracture Section
p.981

Cyclic Softening Properties of 30Cr2MoV Steel at Elevated Temperatures
p.987

A Study on the Corrosion Fatigue Characteristics of 12Cr Alloy Steel
p.993

Corrosion Fatigue Crack Initiation Life of a Ship Structural Steel in Dilute Sulfuric Acids
p.999

An Analysis of Random Fatigue Strength of K-Type Tubular Joints by Probabilistic Fracture Mechanics Method
p.1005

Fatigue Life Prediction of Bolted Joints Using Fatigue Modulus
p.1011

Study of Crack Propagation Behavior on Low Cycle Fatigue in Squeeze Cast Aluminium Alloy
p.1017

Reliability Analysis of Ship Hull Girders Considering the Degradations of Corrosion and Fatigue
p.1023

HomeKey Engineering MaterialsKey Engineering Materials Vols. 183-187Corrosion Fatigue Crack Initiation Life of a Ship...

Corrosion Fatigue Crack Initiation Life of a Ship Structural Steel in Dilute Sulfuric Acids

Article Preview

Abstract:

You might also be interested in these eBooks

Fracture and Strength of Solids IV

Info:

Periodical:

Key Engineering Materials (Volumes 183-187)

Pages:

999-1004

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.183-187.999

Citation:

Cite this paper

Online since:

April 2000

Authors:

Yoshinori Kobayashi, Yasunori Tanaka, H. Goto

Keywords:

Corrosion Fatigue, Crack Initiation, Dilute Sulfuric Acid, Equivalent Stress, Fatigue Life, Notch, Stress Concentration Factor (SCF), Stress Intensity Factor Range (ΔK), Threshold

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 2000 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation: