Effect of Constraint on the Initiation of Ductile Fracture in Shear Loading
p.183

Study on Damage History under the Different Stress Triaxiality in Constrained Ductile Media
p.189

A Robust Method for Ramberg-Osgood Fit Relevant to Elastic-Plastic J Estimates
p.195

Brittle Damage and Coalescence Model of Jointed Rock Mass
p.201

Stable Crack Extension through AISI 4340 Steel: Experimental Investigation
p.207

Experimental Study on Fracture Mechanism of Aluminum Plates in Tension and Laser Irradiation with High Temperature Moiré Interferometry
p.213

The Mechanisms of Crack Propagation from Surface 3-D Fracture under Uniaxial Compression
p.219

A Study of Fracture Mechanism and Shear Strength of Rock Bridges through Analytical and Model-Testing Methods
p.225

Damage Tolerance Analysis of Multiple Cracks Starting from Holes in a Plate Loaded by Bending and Tension
p.231

HomeKey Engineering MaterialsKey Engineering Materials Vols. 261-263Stable Crack Extension through AISI 4340 Steel:...

Stable Crack Extension through AISI 4340 Steel: Experimental Investigation

Article Preview

Abstract:

You might also be interested in these eBooks

Advances in Fracture and Failure Prevention

Info:

Periodical:

Key Engineering Materials (Volumes 261-263)

Pages:

207-212

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.261-263.207

Citation:

Cite this paper

Online since:

April 2004

Authors:

Abdel Hamid I. Mourad, M.G. Alghafri, O.A. Abu Zeid

Keywords:

Crack Growth Through AISI Steel, Stable Crack Growth

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 2004 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation: