Literature Survey on Porosity and Microporosity in Cast Irons Related to Expansion and Gas Entrapment Phenomena

Vitor Anjos; Carlos A. Silva Ribeiro; Fátima Dias; Wolfgang Baumgart; João Cunha

doi:10.4028/www.scientific.net/KEM.457.410

Paper Titles

Effect of Copper Addition on Mechanical Properties of Nodular Indefinite Chilled Iron (NICI)
p.386

Notch Effects on Impact and Bending Characteristics of Spheroidal Graphite and Compacted Vermicular Graphite Cast Irons with Various Matrices
p.392

Effects of Graphite Shape on Thermal Fatigue Property of Thin Wall Graphitic Cast Irons
p.398

Bending Strength of Cast Materials Reinforced with Hard Particles
p.404

Literature Survey on Porosity and Microporosity in Cast Irons Related to Expansion and Gas Entrapment Phenomena
p.410

On the Formation of Shrinkage Porosity in Gray Iron Castings
p.416

Surface Turbulence at Flow of Gray Cast Iron
p.422

Suppression of Elevated Temperature Brittleness in Spheroidal Graphite Cast Iron by Increasing Phosphorus Content
p.428

Selection of Cast Iron Grade for Stub-Anode Fixation in Aluminum Electrolytic Cells
p.435

HomeKey Engineering MaterialsKey Engineering Materials Vol. 457Literature Survey on Porosity and Microporosity in...

Literature Survey on Porosity and Microporosity in Cast Irons Related to Expansion and Gas Entrapment Phenomena

Abstract:

Macro and microporosity in castings are a problem that persists at many foundries, despite the use of advance simulation software’s. This fact indicates that other parameters rather then the casting shape/design or the “standard” metallurgical characteristics are not properly controlled, considered or modelled in the solidification simulation. In this paper we present the Phase I of a research project, which consists on a bibliographic review of the previous attempts to evaluate the relationship between solidification sequence and the measurement of expansion of molten metal during eutectic solidification and is relation to porosity and shrinkage defects.

You might also be interested in these eBooks

View Preview

Info:

Periodical:

Key Engineering Materials (Volume 457)

Pages:

410-415

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.457.410

Citation:

Cite this paper

Online since:

December 2010

Authors:

Vitor Anjos, Carlos A. Silva Ribeiro, Fátima Dias, Wolfgang Baumgart, João Cunha

Keywords:

Influences on Shrinkage, Metallurgical Control, Microporosity, Porosity, Solidification Expansion

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

References

[1] Campbell, John; Castings,; Buttworth Heinmann - Second Edition; 2003; 222 - 231.

Google Scholar

[2] Metals Handbook Volume 15; Casting,; ASM International - Fourth Edition 1198; 1232 - 1244.

Google Scholar

[3] Science and Engineering of Casting Solidification - Doru M. Stefanescu, 2nd Edition, Springer, 2009; 303 - 313.

Google Scholar

[4] I. Ohnaka, A. Sato, A. Sugiyama, F. Kinoshita; Mechanism and estimation of porosity defects in ductile iron,; International Journal of Cast Metals Research, 2008, Vol 21; Nr. 1-4.

DOI: 10.1179/136404608x361585

Google Scholar

[5] Z. Gedeonová, J. Dúl, S. Bódi; Die Bewegung der Grenzfläche Meall/Form während der Erstarrung von Gußeisen mit Kugelgraphit und mit Lamellengraphit, Gießerei-Praxis Nr 7/81996, 150-155.

Google Scholar

[6] Z. Gedeonová, H. Pacyna; "Metallurgische und technologische Einfluß für den Speisungs.

Google Scholar

[7] W. Schmitz, S. Engler; Kunstharzgebundene Formen - Einfluß verschiedener Bindersysteme auf die Metallwand- und Formkastenbewegung,; Gießrei-Praxis Nr 7 - 1994, 132 to 140.

Google Scholar

[8] J. Ferreira, "Tecnologia da Fundição; 2 nd edition, Fundação Calouste Gulbenkian, Lisboa, 2007; 252 and 340.

Google Scholar

[9] R. Hummer, Beurteilung der Lunkerneigung von Gußeisen mit Kugelgraphit mittles Abkühl- und Längenänderungskurven, Giesserei-Praxis Nr. 9/10-1989, 142 to 151.

Google Scholar

[10] S. Karsay, Ductile Iron I - Production,; QIT - Fer et Titane Inc. 1992 ; 153 to 157.

Google Scholar