The Evaluation for In-Service Material Degradation of Superheater Tubes of Fossil Boiler
p.253

DBTT Estimation of Ferritic Low Alloy Steels in Service Plant by means of Small Punch Test
p.259

Fatigue Crack Behavior under Constant Stress and Two-Step Block Stress
p.265

Effect of Single Overload on Retardation Behavior in 7075-T73 Aluminium Alloy
p.271

Estimation Method of Elastic-Plastic Fatigue Crack Growth Rates under Variable Amplitude Loadings
p.277

HomeKey Engineering MaterialsKey Engineering Materials Vols. 51-52The Evaluation for In-Service Material Degradation...

The Evaluation for In-Service Material Degradation of Superheater Tubes of Fossil Boiler

Article Preview

Abstract:

You might also be interested in these eBooks

Fracture and Strength '90

Info:

Periodical:

Key Engineering Materials (Volumes 51-52)

Pages:

253-258

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.51-52.253

Citation:

Cite this paper

Online since:

January 1991

Authors:

Jung Kyu Kim, T.R. Chung, Jae Kyoo Lim, Se Hi Chung

Keywords:

CVN Energy, Ductile-Brittle Transition Temperature (DBTT), Fracture Appearance Transition Temperature FATT, GEM, Material Degradation, Small Punch SP, ΔDBTT Shift of DBTT, ΔFATT Shift of FATT

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

© 1991 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation: