Preparation and Property Characterization of Talc/Phthalocyanine Blue Composite Powder

Abstract:

To improve the dispersion of phthalocyanine blue powder, decrease its consumption and increase the use value of talc, TPBCP (Talc / Phthalocyanine Blue Composite Powder) was prepared by liquid phase mechanochemical method. By means of paint performance test, scanning electron microscopy (SEM) and fourier transform infrared spectroscopy (FT-IR), the properties and microstructure of composite powder were characterized. The hiding power and oil absorption value of talc/phthalocyanine blue composite powder were 12.88 g/m2 and 32.50 g/100g respectively, and the International Commission on Illumination (CIE) colorimetric data L, a, and b were 44.95, 1.65 and -17.18 respectively. It was equivalent for the hiding power of composite powder to 77.6% of that of pure phthalocyanine blue with a equivalent CIE. The formation of TPBCP was marked by phthalocyanine blue particles uniformly coated on talc surface. The results showed that TPBCP had similar performances with phthalocyanine blue and could instead of phthalocyanine blue to be applied in several fields.

• Periodical: Key Engineering Materials (Volumes 512-515)
• Pages: 239-244
• DOI: https://doi.org/10.4028/www.scientific.net/KEM.512-515.239
• Online since: June 2012
• Authors: Yun Xing Zheng, Hao Ding, Le Fu Mei, Xi Yao Zhu, Meng Meng Wang
• Keywords: Coat, Composite Powder, Mechanism, Mechanochemistry, Phthalocyanine Blue, Talc

References

[1] Y. J. Shen, et al: Organic pigments - varieties and applications, Chem Ind Press, Beijing, 2007.

[2] W. X. Hou, J. R. Tan, X. S. Fu, et al: Preparation of phthalocyanine blue-active carbon coated mica-based pearlescent pigment, J. Paint & Coating Industry. 5 (2002), pp.22-24

[3] N. Bulychev, O. Confortini, P. Kopold, et al: Application of thermo-responsive poly (methyl vinyl ether) containing copolymers in combination with ultrasonic treatment for pigment surface modification in pigment dispersions, J. Polymer. 48 (2007), pp.2636-2643

DOI: 10.1016/j.polymer.2007.02.052

[4] A. Krysztafkiewicz, S. Binkowski, I. Wysocka: Pigments on amorphous silica carriers, J. Powder Technol. 132 (2003), pp.190-195

DOI: 10.1016/s0032-5910(03)00073-1

[5] Y. Z. Lin, H. Z. ShengJin. JPN. Patent 02122251.7 (2001)

[6] H. Ding, Y. X. Deng and G. X. Du: Effect of surface coating TiO2 on the properties of CaCO3/TiO2 composite material as a pigment, J. Funct. Mater. 38 (2007) pp.2495-2498

[7] H. Ding, Y. P Zha, R. C. Ren: Research on component and microcosmic form of tourmaline /TiO2 composite material, J. Journal of Liaoning Technical University. 26 (2007) pp.188-190

[8] X. Q. Wang, L. L. Wei: Grafting metal phthalocyanine onto the cellulose fiber and its deodorizing effect, J. Journal of Textile Research. 27 (2006) pp.5-7