The Effect of Sintering Profiles on Zirconia Toughened Alumina (ZTA) Prepared by Two-Stage Sintering

Abstract:

The effects of sintering profiles on the Zirconia Toughened Alumina (ZTA) composite containing 0 vol% Y-TZP (pure alumina) to 20 vol% Y-TZP content prepared by a sintering method known as two-stage sintering were investigated. The heating rate was set between 10°C/min to 20°C/min, T₁ set between 1400°C to 1500°C, T₂ at 1350°C and holding time was set at 12 hours. The samples’ microstructural properties and mechanical properties, including bulk density, Vickers hardness, Young’s modulus and fracture toughness, were evaluated. Based on the data obtained, the ZTA composites with 10 vol% Y-TZP sintered at a heating rate of 10°C/min and holding time of 12 hours were able to achieve mechanical properties requirements set by the industry standard. In addition, the maximum ZTA composite’s bulk density was recorded to be above 90% T.D, while the Vickers hardness of the composite was recorded to be exceeding 17 GPa. The ZTA composite also recorded maximum Young’s modulus exceeding 380 GPa and fracture toughness above 6 MPam^1/2.

• Periodical: Key Engineering Materials (Volume 904)
• Pages: 174-180
• DOI: https://doi.org/10.4028/www.scientific.net/KEM.904.174
• Online since: November 2021
• Authors: Teow Hsien Loong*, Sivakumar Sivanesan, Se Yong Eh Noum
• Keywords: Sintering Profiles, Two-Stage Sintering, Zirconia Toughened Alumina, ZTA

References

[1] S. Sivakumar, S. Ramesh, K.L. Chin, C.Y. Teng, Effect of sintering profiles on the properties of ageing resistance of Y-TZP ceramic. Int. Jour. of Auto. and Mech. Eng., 4, (2011) 405-413.

DOI: 10.15282/ijame.4.2011.3.0033

[2] M. M. Hossen, F. U. Z. Chowdhury, M. A. Gafur, A. A. Hakim, & M. B. Hossen, Effect of zirconia substitution on structural and mechanical properties of ZTA composites. Jour. of Mech. and Civ. Eng., 11 no. 2 (2014) 01-07.

DOI: 10.9790/1684-11210107

[3] S. Sequeira, M.H. Fernandes, N. Neves, M. M. Almeida, Development and characterization of zirconia-alumina composites for orthopedic implants, Ceram. Int., 43 no. 1 (2017) 693-703.

DOI: 10.1016/j.ceramint.2016.09.216

[4] F. Kern, P. Palmero, F.G. Marro, A. Mestra, Processing of alumina-zirconia composites by surface modification route with enhanced hardness and wear resistance, Ceram. Int., 41 no. 1 (2015) 889-898.

DOI: 10.1016/j.ceramint.2014.09.006

[5] M. Boniecki, P. Golebiewski, W. Wesolowski, M. Woluntarski, A. Piatkowska, M. Romaniec, P. Ciepielewski, K. Krzyzak, Alumina/zirconia composites toughened by the addition of graphene flakes, Ceram. Int., 43 no. 13 (2017) 10066-10070.

DOI: 10.1016/j.ceramint.2017.05.025

[6] T.H. Loong., S.Y. Eh Noum, W.W. Mun, Two-Stage Sintering of Nb2O5 Doped Zirconia Toughened Alumina (ZTA) Composites, K.E.M., 861 (2020) 327-333.

DOI: 10.4028/www.scientific.net/kem.861.327

[7] J. Chen, Z. Xie, W. Zeng, & W. Wu, Toughening mechanisms of ZTA ceramics at cryogenic temperature (77 K). Ceram. Int., 43 no.5 (2017) 3970-3974.

DOI: 10.1016/j.ceramint.2016.11.072

[8] A. Arab, A. Z. Ahmad, & R. Ahmad, Effects of yttria stabilized zirconia (3Y-TZP) percentages on the ZTA dynamic mechanical properties. Int. Jour. of Refrac. Metals and Hard Mat., 50 (2015) 157-162.

DOI: 10.1016/j.ijrmhm.2015.01.005

[9] T.H. Loong., S.Y. Eh Noum, W.W. Mun, The Effect of Ta2O5 on the Densification Behaviour and Mechanical Properties of Zirconia-Toughened Alumina (ZTA) Composites Prepared by Two-Stage Sintering. K.E.M., 861 (2020) 320-326.

DOI: 10.4028/www.scientific.net/kem.861.320

[10] W.H. Tuan, R. Z. Chen, T.C. Wang, C.H. Cheng, P.S. Kuo, Mechanical Properties of Al2O3/ZrO2 composites, J. of the Eur. Ceram. Soc., 22 no. 16 (2002), 2827-2833.

DOI: 10.1016/s0955-2219(02)00043-2

[11] G.K.R. Pereira, M. Amaral, P.F. Cesar, M.C. Bottino, C.J. Kleverlaan& L.F. Valandro, Effect of low-temperature aging on the mechanical behavior of ground Y-TZP. Jour. of the mech. Beh. of biomed. Mat., 45 (2015) 183-192.

DOI: 10.1016/j.jmbbm.2014.12.009

[12] I.W. Chen, X.H. Wang, Sintering dense nanocrystalline ceramics without final-stage grain growth, Nature, 404 no. 6774 (2000) 168.

DOI: 10.1038/35004548

[13] S. Sivanesan, T. H. Loong, S. Namasivayam, M. H. Fouladi, Two-Stage Sintering of Alumina-Y-TZP (Al2O3 /Y-TZP) Composites, K.E.M., 814 (2019) 12-18.

DOI: 10.4028/www.scientific.net/kem.814.12

[14] Y. I. Lee, Y. W. Kim, M. Mitomo, D. Y. Kim, Fabrication of dense nanostructured silicon carbide ceramics through two-step sintering, J. of the Am. Ceram. Soc., 86 no. 10 (2003) 1803-1805.

DOI: 10.1111/j.1151-2916.2003.tb03560.x

[15] A. Polotai, K. Breece, E. Dickey, C. Randall, A. Ragulya, A Novel Approach to Sintering Nanocrystalline Barium Titanate Ceramics, J. of the Am. Ceram. Soc., 88 no. 11 (2005) 3008-3012.

DOI: 10.1111/j.1551-2916.2005.00552.x

[16] K. Niihara, A fracture mechanics analysis of indentation-induced Palmqvist crack in ceramics, J. of. Mater. Sci. Letters, 2 no. 5 (1983) 221-223.

DOI: 10.1007/bf00725625

[17] M. Mazaheri, A. Simchi, M. Dourandish, F. J. Golestani-Fard, Master Sintering Curves of a Nanoscale 3Y-TZP powder compacts, Ceram. Int., 35 no. 2 (2009) 547-554.

DOI: 10.1016/j.ceramint.2008.01.008

[18] G. Bernard-Granger & C. Guizard, Apparent Activation Energy For The Densification Of a Commercially Available Granulated Zirconia Powder, J. Am. Ceram. Soc.,90 no. 4, 1246-1250.

DOI: 10.1111/j.1551-2916.2006.01415.x

[19] A. M. Hassan, S. M. Naga, M. Awaad, Toughening and strengthening of Nb2O5 doped zirconia/alumina (ZTA) composites, Int. Jour. of Refrac. Met. and Hard Mater., 48 (2015) 338-345.

DOI: 10.1016/j.ijrmhm.2014.10.006

[20] V. Naglieri, P. Palmero, L. Montanaro, J. Chevalier, Elaboration of alumina-zirconia composites: Role of zirconia content on the microstructure and mechanical properties, Materials, 6 no. 5, 2090-2102.

DOI: 10.3390/ma6052090

[21] A. Moradkhani, H. Baharvandi, Effects of additive amount, testing method, fabrication process and sintering temperature on the mechanical properties of Al2O3/Y-TZP composites, Eng. Frac. Mech., 191 (2018) 446-450.

DOI: 10.1016/j.engfracmech.2017.12.033