Self-Sensing Capabilities of Cement Pastes Treated by Direct Current Curing Technique

Abstract:

In this study, an innovative curing technique, that is able to polarize the ions inside cement pastes is investigated. This technique is curing the cement paste while applying a direct current (DC). A total of 6 cement paste cubes were casted, 3 of them were not treated so it will serve as a reference and other 3 were cured while applying 25 V DC on two opposite sides of the specimen. All specimens were tested under different amplitude cyclic loading and the produced piezoelectric voltage was recorded. The results show that this technique was able to increase the produced piezoelectric voltage of the treated cement paste specimens when compared to the reference ones. In addition, the produced piezoelectricity showed a proportional behavior to the applied loads, which indicates the capabilities of self-sensing of the treated specimens. The voltage sensitivity values of the both the reference specimens and the treated ones are 0.34 and 1.77 mV/kN, respectively. The effect of the trapped moisture inside the specimens was also investigated, and the results show that the piezoelectricity greatly depends on the existence of moisture inside the specimens.

• Periodical: Materials Science Forum (Volume 1060)
• Pages: 201-205
• DOI: https://doi.org/10.4028/p-vvo5zv
• Online since: May 2022
• Authors: Mohammad Al-Qaralleh*
• Keywords: Piezoelectricity of Cement Pastes, Polarized Cement Paste, Self-Sensing Cement Hydrates, Structural Health Monitoring

References

[1] H. Elahi, M. Eugeni, P. Gaudenzi, A review on mechanisms for piezoelectric-based energy harvesters, Energies. 11 (2018). https://doi.org/10.3390/en11071850.

DOI: 10.3390/en11071850

[2] M. Sun, Q. Liu, Z. Li, Y. Hu, A study of piezoelectric properties of carbon fiber reinforced concrete and plain cement paste during dynamic loading, 30 (2000) 1593–1595.

DOI: 10.1016/s0008-8846(00)00338-0

[3] S. Yeol, H. Viet, D. Joo, Self-stress sensing smart concrete containing fine steel slag aggregates and steel fibers under high compressive stress, Constr. Build. Mater. 220 (2019) 149–160. https://doi.org/10.1016/j.conbuildmat.2019.05.197.

DOI: 10.1016/j.conbuildmat.2019.05.197

[4] A.J. Al-Bayati, K. Butrouna, S. Robert, B. Salman, M. Al-Qaralleh, Utilizing Graphite Powder to Improve Concrete Conductivity, Compressive Strength, and Workability, Constr. Res. Congr. 2020. (2021) 881–888. https://doi.org/.

DOI: 10.1061/9780784482889.093

[5] I.B. Topu, T. Uygunolu, I. Hocaolu, Electrical conductivity of setting cement paste with different mineral admixtures, Constr. Build. Mater. 28 (2012) 414–420. https://doi.org/10.1016/j.conbuildmat.2011.08.068.

DOI: 10.1016/j.conbuildmat.2011.08.068

[6] Z. Tian, Y. Li, J. Zheng, S. Wang, A state-of-the-art on self-sensing concrete : Materials , fabrication and properties, Compos. Part B. 177 (2019) 107437. https://doi.org/10.1016/j.compositesb.2019.107437.

DOI: 10.1016/j.compositesb.2019.107437

[7] Y.L. Yaphary, S. Hu, D. Lau, R.H.W. Lam, Piezoelectricity of Portland cement hydrates cured under the influence of electric field, 16th Int. Conf. Nanotechnol. - IEEE NANO 2016. (2016) 911–914. https://doi.org/10.1109/NANO.2016.7751344.

DOI: 10.1109/nano.2016.7751344

[8] M. Al-Qaralleh, Effect of Water Cement Ratio on the Electrical Conductivity and Piezoelectricity of Cement Paste Cured While Applying Direct Current, Mutah Resesrch Stud. Nat. Appl. Sci. (In press).

[9] ASTM C305–06, Standard Practice for Mechanical Mixing of Hydraulic Cement Pastes and Mortars of Plastic Consistency, ASTM Int. 04 (2009) 3. https://www.astm.org/Standards/C305.

DOI: 10.1520/c0305-99