Corrosion Protection of AISI 304 Stainless Steel Filters by a Surface Treatment

Abstract:

In this study a corrosion protection method was used with AISI 304 SS filters and its effect on their corrosion resistance was evaluated in a sodium chloride solution (0.5 mol/L). The corrosion resistance of the surface treated filters was investigated at increasing temperatures, from 22 oC to 100 oC. It was found that the treatment improved the corrosion resistance of the filters at all temperatures tested. The film formed was maintained on the filters surface during the whole period of test (3 weeks). Surface analysis of untreated and treated filters, after corrosion tests, supported the indication of the beneficial effect of the corrosion protection treatment evaluated in this study.

• Periodical: Materials Science Forum (Volumes 498-499)
• Pages: 93-97
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.498-499.93
• Online since: November 2005
• Authors: L. De Micheli, Isolda Costa
• Keywords: BTAH, Corrosion, Sintered Stainless Steel Filters, Surface Films

References

[1] S. N. Molhotra, P. Ramakrisshnan. MPR, 46, no 11 (1991), p.48.

[2] A. L. Müller. Powder Metallurgy International, 14, no 2 (1982).

[3] E. Otero, A. Pardo, V. Utrilla, E. Sàenz, F. J. Pérez. 12th International Corrosion Congress. Corrosion Specific Issue, vol. 3B (1993), p. (2037).

[4] F. Veslasco, J. R. Ibars, J. M. Ruiz-Roman, J. M. Torralba, J. M. Ruiz-Prieto. Corrosion, 52 n o 1 (1996), p.47.

[5] D. Itzhak, E. Eghion. Corrosion Science, 24, no 2 (1984), p.145.

[6] E. Otero, A. Pardo, E. Saenz, M. V. Utrilla, P. Hierro. Corr. Science, 38, no 9 (1996), p.1485.

[7] E. Otero, A. Pardo, M. V. Utrilla, F. J. Perez, C. Merino. Corr. Science, 39, no 3 (1997), p.453.

[8] L. Fedrizzi, F. Deflorian, A. Tiziani. Advances in Powder Metallurgy & Particulata Materials, 7 (1994), p.273.

[9] E. Maahn, S. K. Jensen, R. M. Larsen, T. Mathiessen. Advances in Powder Metallurgy & Particulate Materials, (1994), p.253.

[10] T. Raghu, S. N. Malhorta, P. Ramakrishnan. British Corrosion Journal, 2 (1988), p.109.

[11] P. Peled, S. Harush and D. Itzhak, Corr. Sci., 28 (4), 327, (1988).

[12] A. Sharon, N. Melman, and D. Itzhak, Powder Metallurgy 37 (1), 67, (1994).

[13] T. Mathiesen and E. Maahn. Advances in Powder Metallurgy and Particulate Materials, 3 (1995), p.45.

[14] L. Fedrizzi, F. Deflorian, A. Tiziani, I. Cristofolini, A. Molinari. Advances in Powder Metallurgy and Particulate Materials, 7 (1994), p.273.

[15] A. Tremblay and R. Angers. Advances in Powder Metallurgy and Particulate Materials, 7 (1995), p.225.

[16] P. R. P. Rodrigues, I. V. Aoki, A. H. P. Andrade, S. M. L. Agostinho. British Corrosion Journal, 31 (1996), p.305.

[17] L. De Micheli; A. H. P. Andrade, C. A. Barbosa, S. M. L. Agostinho. British Corrosion Journal, 34 (1999), p.67.

[18] L. De Micheli; A. H. P. Andrade, C. A. Barbosa, S. M. L. Agostinho. British Corrosion Journal 35 (2000), p.297.

[19] P. R. P. Rodrigues, Benzotriazole as corrosion inhibitor for iron and ferrous alloys in sulphuric acid media, Doctorate thesis, USP, Instituto de Quimica, 1997, 219p (In Portuguese).

[20] L. De Micheli, I. Costa, Materials Science Forum, 416-418 (2003) p.70.