Study on the Precursory Powder for Bi-2223 Tape

Abstract:

Article Preview

The Phase formation in the precursory powder, the particle size and the homogenization phase distribution have been investigated in this paper. Size of the powder particle has been reduced by a ball-milling process. The effects of the ball-milling on the characteristic of the powder have been studied by XRD. The modality and distribution of 2212, Ca2CuO3 and CuO in the powder were observed by SEM. Results show that the Ca2CuO3 particle ground was about 200nm in size. The precursory powder with the non-superconducting phases distributed uniformly in the mixture powder was obtained for Bi-2223 long tape.

Info:

Periodical:

Materials Science Forum (Volumes 546-549)

Edited by:

Yafang Han et al.

Pages:

1961-1966

Citation:

H.L. Zheng et al., "Study on the Precursory Powder for Bi-2223 Tape", Materials Science Forum, Vols. 546-549, pp. 1961-1966, 2007

Online since:

May 2007

Export:

Price:

$38.00

[1] R M Baurceanu, V A Maronil, N M Merchantl, A K Fischer, M J McNallan and R D Parrella Supercond. Sci. Technol. 15(July 2002) 116-1175.

[2] S.E. Dorris, B.C. Prorok, M.T. Lanagan, S. Sinha, R.B. Poeppel Physica C vol. 212 No. 1&2 1993 pp.66-250.

[20] [40] [60] [80] 100 120 77K, self field critical current (A) lenght (m ) B0428 Ave=82. 69 s=4. 415.

5 0 100 1 50 2 00 250.

[5] [10] [15] [20] [25] n-value le n g th (m ) E 0 4 -2 8 (a) (b) Figure 7. Critical current (Ic) uniformity along length of Bi-2223 tapes in (a) (Ic at 1µV/cm); (b) n-value. (Data are obtained for each 27m section. ) (a) (b) Figure 6. Distribution of Ca2CuO3 and CuO particles in the mixing powder after different processes. More homogeneous Ca-Cu-O particle distribution in (a) by an optimum process;  Little conglomerations of Ca-Cu-O powder in (b) by an previous process. [3] T.G. Holesinger, K.V. Salazar, D.S. Phillips, B.L. Surgent, J.K. Bremser, J.Q. Willis, D.E. Peterson J. Mater. Res. Vol. 11 No. 1 1996 pp.28-38.

DOI: https://doi.org/10.1557/jmr.1996.0005

[4] R Flukiger, G Grasso, J C Grivel, F Marti, M Dhalle and Y Huang Supercond. Sci. Technol. 10(1997) A 68-A92.

[5] C.H. Jiang, J.M. Yoo, J.W. Ko, H.S. Chung and G.W. Qiao Supercond. Sci. Technol. 16(2003) 85-89.

[6] E. Guimean, D. Chaterigner and J.G. Noudem Supercond. Sci. Technol. 16(2003)484-491.

[7] Zheng Huiling et at PROCEEDINGS OF ICETS 2000-ISAM Chinese Academy of Engineering October 11. 2000 Beijing China New World Press.

[8] SECUTITY OF POWER SYSTEM AND SUPERCONDUCTING MAGNETIC ENERGY STORAGE Shi Jing et at CHINESE JOURNAL OF LOW TEMPERATURE PHYSICS Vol. 27 No. 5 Nov. 2005 pp.1051-1056.

Fetching data from Crossref.
This may take some time to load.