Microstructures and Mechanical Properties of TiAl-Based Alloys Prepared by High-Energy Ball Milling and Hot-Pressing Sintering

Article Preview

Abstract:

TiAl-based alloy with a composition of Ti-47%Al-3%Cr (mole fraction) was prepared by high-energy ball milling and hot-pressing sintering. The relationship between microstructure and mechanical properties of Ti-47%Al-3%Cr alloy was studied by X-ray diffractometry (XRD), scanning electron microscopy (SEM) and mechanical testing. The results showed that the TiAl-based alloy with high density and uniform microstructure could be obtained by high-energy ball milling and hot-pressing sintering. The compactibility and sintering densification of the element powder could be promoted efficiently by high-energy ball milling. The main phase TiAl and few phases Ti3Al were observed in the hot pressing sintering bulk samples. In addition, the microstructure changed with ball milling times, as a result, the mechanical properties changed with the microstructure. The finer the microstructure was, the higher the strength at room temperature became. After the element powder was milled for 20 hours and hot-pressing sintered at 1300 °C for 2 hours, TiAl-based alloys were found to have good room temperature mechanical properties with the compressive strength of 2870 Mpa and the relative compressive ratio of 27.3%. Keywords: TiAl-based alloys; hot-pressing sintering; microstructure; mechanical properties

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volumes 704-705)

Pages:

828-831

Citation:

Online since:

December 2011

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2012 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] L. M. Hsiung and T. G. Nieh: Mater. Sci. Eng. A Vol. 364(2004), p.1.

Google Scholar

[2] R. Gerling, E. Aust, W. Limberg, M. Pfuff and F. P. Schimansky: Mater. Sci. Eng. A Vol. 423(2006), p.262.

Google Scholar

[3] W. Maziarz, A. Michalski, P. Kurtyka and J. Dutkiewicz: Rev. Adv. Mater. Sci. Vol. 8(2004), p.158.

Google Scholar

[4] S. L. Xiao, J. Tian, L. J. Xu, Y. Y. Chen, H. B. Yu and J. C. Han: Trans. Nonferrous Met. Soc. China, Vol. 19(2009), P. 1423.

Google Scholar

[5] N. Forouzanmehr, F. Karimzadeh and M. H. Enayati: J. Alloys Compd. Vol. 471(2009), p.93.

Google Scholar

[6] A. Nouri, X. B. Chen, Y. C. Li, Y. Yamada, P. D. Hodgson, C. Wen: Mater. Sci. Eng. A Vol. 485(2008), p.562.

Google Scholar

[7] Z. M. Sun, Q. Wang, H. Hashimoto, S. Tada and T. Abe: Intermet. Vol. 11(2003), p.63.

Google Scholar

[8] W. B. Fang, L. X. Lian, W. X. He, E. D. Wang and X. Q. Li: Mater. Sci. Eng. A Vol. 403(2005), p.186.

Google Scholar

[9] P. Bhattacharya, P. Bellon, R. S. Averback and S. J. Hales: J. Alloys Compd. Vol. 368(2004), p.187.

Google Scholar

[10] Y. Liu, B. Y. Huang and Y. H. He: Trans. Nonferrous Met. Soc. China, Vol. 10(2000), P. 453.

Google Scholar

[11] M. R. Farhang, A. R. Kamali and M. N. Samani: Mater. Sci. Eng. B Vol. 168(2010), p.136.

Google Scholar

[12] L. Lu, M. O. Lai, Y. H. Toh and L. Froyen: Mater. Sci. Eng. A Vol. 334(2002), p.163.

Google Scholar