Effect of Annealing Process on Mechanical Properties and Texture Changes of AZ31 Mg Alloy Sheets

Abstract:

Article Preview

Mg alloy sheets exhibit the yield strength of 280 MPa and elongation of 18 % by rolling at 423 K. Elongation of Mg alloy sheets was improved up to 35 % when the sample was annealed at 673 K for 10 min. From the observation of microstructure, recrystallization and grain growth have happened during annealing processes. The intensity of 0002 pole figure increases slightly as a function of annealing temperature.

Info:

Periodical:

Edited by:

Jing Sun, Lian Gao, Hyungsun Kim, Jian Feng Yang, Tohru Sekino and Soo Wohn Lee

Pages:

190-193

DOI:

10.4028/www.scientific.net/MSF.724.190

Citation:

H. J. Bang et al., "Effect of Annealing Process on Mechanical Properties and Texture Changes of AZ31 Mg Alloy Sheets", Materials Science Forum, Vol. 724, pp. 190-193, 2012

Online since:

June 2012

Export:

Price:

$38.00

[1] I.J. Polmear, Mater. Sci. Tech. 10 (1994) 1-16.

[2] S.R. Agnew, J.A. Horton, T.M. Lillo, D.W. Brown, Scripta Mater. 50 (2004) 377-381.

[3] H.K. Lin, J.C. Huang, T.G. Langdon, Mate. Sci. Eng. A 402 (2005) 250-257.

[4] Masaaki kai, Zenji Horita, Terence G Langdon, Mater. Sci. Eng. A 488 (2008) 117-127.

[5] H. Koh, T. Sakai, H. Utsunomiya, S. Minamiguchi, Mater. Trans. 48 (2007) 2023-(2027).

[6] J.B. Lee, T.J. Konno, H.G. Jeong, Mater. Sci. Eng B 161 (2009) 166-169.

In order to see related information, you need to Login.