Process Optimization and Microstructure Control for Twin Screw Rheo-Extrusion of an AZ91D Magnesium Alloy

Abstract:

Twin screw rheo extrusion (TSRE) is a continuous semisolid forming process. The process takes advantage of the thixotropic properties of semisolid metal slurry and the high shear, controllable forward driving and self-sweeping capabilities of a counter rotating twin screw mechanism, offering a one-step melt-to-product forming technology with significant savings on energy consumption and manufacturing cost. The present work was carried out to investigate the feasibility of the process for processing light alloys using an AZ91D magnesium alloy and to obtain optimized operation conditions for microstructure control. A range of processing parameters was tested for slurry making, feeding and extrusion and their effect on microstructure development was examined. Experimental results showed that slurry with non-dendritic primary phase particles of various volume fractions, typical of semisolid microstructure, was obtained prior to extrusion. The particles were further refined during extrusion due to dynamic shearing applied by the twin screw mechanism under controlled thermal schemes and the final microstructure obtained after extrusion was dominated by uniformly distributed equiaxed, non-dendritic spherical grains and the average grain size was in the range of 35-80 mm, depending on processing parameters. This paper presents the performance of the TSRE process, focussing on process optimization and microstructure control. Mechanisms of microstructural refinement and particle morphology evolution are discussed.

• Periodical: Materials Science Forum (Volume 765)
• Pages: 439-443
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.765.439
• Online since: July 2013
• Authors: Zen Cassinath, Ming Xu Xia, Huang Yan, Zhong Yun Fan
• Keywords: Magnesium Alloy, Mechanical Behavior, Microstructural Evolution, Rheo-Extrusion, Semi-Solid Processing

References

[1] D. Pinsky, P. Charreyron, M. Flemmings, Compression of semisolid dendritic Sn-Pb alloys at low strain rates, Metall. Trans. B 15 (1984) 173-181.

DOI: 10.1007/bf02661076

[2] F. Czerwinski, Semisolid extrusion moulding of Mg-9%Al-1%Zn alloys, J. Mat. Sci. 39 (2004) 463-468.

DOI: 10.1023/b:jmsc.0000011499.82960.9d

[3] B. Lee, D. Joo, M. Kim, Extrusion behaviour of Al-Cu alloys in the SS state, J. Mat. Sci. Eng. A 401 (2005) 170-176.

[4] S. Kim, Y. Yoon, H. Jo, Thixoextrusion process for wrought alloys, Mater. Process. Tech. 187 (2007) 354-357.

DOI: 10.1016/j.jmatprotec.2006.11.177

[5] R. Kopp, H. Mertons, M. Wimmer, Thixoextrusion of Aluminium Wrought Alloys C. in: 5th Int. Conf. on SSP of Alloys and Composites, 1998.

[6] M. Flemmings, Behaviour of Metal Alloys in Semisolid state, Metall. Trans. A 22 (1991) 957-981.

[7] A. Vogel, B. Cantor, Stability of a spherical particle growing from a stirred melt, J. Cryst. Growth 37 (1977) 309-316.

DOI: 10.1016/0022-0248(77)90125-7

[8] A. Hellawell, in: 4th Int Conf on SSP of Alloys and Composites (1996) 60-66.

[9] R. Doherty, H. Lee, E. Feest, Microstructure of Stir cast metals, Mat. Sci. Eng. 65 (1984) 181-189.

DOI: 10.1016/0025-5416(84)90211-8

[10] J. Molenaar, F. Salemans, L. Katgerman, The structure of stircast Al-6Cu, J. Mat. Sci. 20 (1985) 4335-4342.

DOI: 10.1007/bf00559322

[11] J. Molenaar, L. Katgerman,W. Kool, On the formation of the stir cast structure, J. Mat. Sci. 21 (1986) 389-394.

[12] A. Mullis, Growth induced dendritic bending and rosette formation during solidification in a shearing flow, Acta Mater. 47 (1999) 1783-1782.

DOI: 10.1016/s1359-6454(99)00052-x

[13] S. Ji, Z. Fan, Solidification behaviour of Sn-15 Wt Pct Pb Alloy under a high shear rate and high intensity of turbulence during semisolid processing, Metall. Trans. A 33 (2002) 3511.

DOI: 10.1007/s11661-002-0338-4

[14] Z. Fan, G. Liu, Solidification behaviour of AZ91D alloy under intensive forced convection in the RDC process, Acta Mater. 53 (2005) 4345-4357.

DOI: 10.1016/j.actamat.2005.05.033

[15] A. Das, S. Ji, Z. Fan, Morphological development of solidification structures under forced fluid flow: a Monte-Carlo simulation, Acta Mater. 50 (2002) 4571–4585.

DOI: 10.1016/s1359-6454(02)00305-1

[16] R. Qin, E. Wallach, Phase-field simulation of semisolid metal processing under conditions of laminar and turbulent flow, Mat. Sci. Eng. A 357 (2003) 45-54.

DOI: 10.1016/s0921-5093(03)00380-0

[17] X. Du, E. Zhang, Microstructure and mechanical behaviour of semi-solid die-casting AZ91D magnesium alloy, Mater. Letts. 61 (2007) 2333-2337.

DOI: 10.1016/j.matlet.2006.09.007

[18] F. Czerwinski, A. Zielinska-Lipieca, P. Pinet, Correlating the microstructure and the tensile properties of a thixomouldedAZ91D Mg Alloy, Acta Mater. 49 (2001) 1225-1235.

DOI: 10.1016/s1359-6454(01)00015-5