Residual Stresses in Rail-Ends from the in-Service Insulated Rail Joints Using Neutron Diffraction

Abstract:

Insulated rail joints (IRJs) are an integral part of the rail track signaling system and pose significant maintenance and replacement costs due to their low and fluctuating service lives. Failure occurs mainly in rail head region, bolt- holes of fishplates and web-holes of the rails. Propagation of cracks is influenced by the evolution of internal residual stresses in rails during rail manufacturing (hot-rolling, roller-straightening, and head-hardening process), and during service, particularly in heavy rail haul freight systems where loads are high. In this investigation, rail head accumulated residual stresses were analysed using neutron diffraction at the Australian Nuclear Science and Technology Organisation (ANSTO). Two ex-service two head-hardened rail joints damaged under different loading were examined and results were compared with those obtained from an unused rail joint reference sample in order to differentiate the stresses developed during rail manufacturing and stresses accumulated during rail service. Neutron diffraction analyses were carried out on the samples in longitudinal, transverse and vertical directions, and on 5mm thick sliceed samples cut by Electric Discharge Machining (EDM). For the rail joints from the service line, irrespective of loading conditions and in-service times, results revealed similar depth profiles of stress distribution. Evolution of residual stress fields in rails due to service was also accompanied by evidence of larger material flow based on reflected light and scanning electron microscopy studies. Stress evolution in the vicinity of rail ends was characterised by a compressive layer, approximately 5 mm deep, and a tension zone located approximately 5- 15mm below the surfaces. A significant variation of d0 with depth near the top surface was detected and was attributed to decarburization in the top layer induced by cold work. Stress distributions observed in longitudinal slices of the two different deformed rail samples were found to be similar. For the undeformed rail, the stress distributions obtained could be attributed to variations associated with thermo-mechanical history of the rail.

• Periodical: Materials Science Forum (Volumes 768-769)
• Pages: 741-746
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.768-769.741
• Online since: September 2013
• Authors: Vladimir Luzin, C. Rathod, D. Wexler, Paul Boyd, Manicka Dhanasekar
• Keywords: Accumulated Stress, Insulated Rail Joints, Neutron Diffraction, Pearlitic Steel, Rail Head, Residual Stress

References

[1] Y. Hiroto: Development of a long life Insulated Rail Joint, Quarterly reports of the Railway Technical Research, Vol. 25 (1984) p.79.

[2] C. Smalley: Preliminary study into fatigue of Insulated Rail Joints, Institute of Railway Technology at Monash University, (2009).

[3] J. Igwemezie, A.T. Nguyen: Anatomy of joint bar failures II, Railway Track & Structures, Vol. 105, Issue 10, (Oct 2009) p.43.

[4] C. Rathod, D. Wexler, T. Chandra, and H. Li, Microstructural characterisation of railhead damage in insulated rail joints, Materials Science Forum Vols. 706-709 (2012) p.2937.

DOI: 10.4028/www.scientific.net/msf.706-709.2937

[5] T. Gnaupel-Herold, P.C. Brand, H.J. Prask, Neutron Diffraction Investigation of Risidual Stresses in Transverse/Oblique Rail Slices Subjected to Different Grinding Stratagies, Report NISTIR 6305, U.S. Department of Commerce, Technology Administration (1999).

DOI: 10.6028/nist.ir.6305

[6] P.J. Webster, K.S. Low, G. Mills, and G.A. Webster, Neutron Measurementsof Residual Stresses in a Used Raiway Rail, Mat. Res. Soc Symp. Proc., 166, (1990) 311-316.

DOI: 10.1557/proc-166-311

[7] G.A. Webster, P.J. Webster, M.A.M. Bourke, K.S. Low, G. Mills, H.J. McGillivray, D.F. Cannon and R.J. Allen, 1992, Neutron Diffraction Determinations of Residual Stress Patterns in Railway Rails, Mat. Res. Soc Symp. Proc 166, (1990) 143-152.

DOI: 10.1007/978-94-011-2797-4_43

[8] V. Luzin, J.E. Gordon, T. Gnaupel-Herold and H.J. Prask, Neutron residual stress measurements on rail sections for different production conditions, Proc. IMECE04, 2004 ASME Int Mech Eng Congr. And Expn, Nov 13-20 (2004), Anaheim, CA, USA, 1-25.

DOI: 10.1115/imece2004-61754

[9] J. Tillberg, F. larson, K. Runesson, A study of multiple crack interaction at rolling contact fatigue loading of rails, Proc. I. Mech E Part F: J. Rail and Rapid Transit, 223 (2009) 319-330.

DOI: 10.1243/09544097jrrt242