Comparative Study of Microstructural and Corrosion Characteristics of Excimer Laser-Melted AA2124-T4 and AA6061-T4 Alloys

Abstract:

A KrF excimer laser was introduced for laser surface melting (LSM) of the aluminium alloys AA2124-T4 and AA6061-T4. The microstructural and compositional analysis was conducted using SEM, low-angle XRD, and TEM; the corrosion behaviour of as-received (AR) and laser-treated (LT) samples was evaluated by electrochemical techniques and immersion test in a 3.5% NaCl solution. A melted layer consisting of a re-solidified layer with refined microstructure and dissolution of intermetallic particles (IMPs), and a thin film of aluminium oxides at the top, was formed after LSM for both alloys. The corrosion resistance of both alloys was improved after LSM. The results of immersion test showed different corrosion behaviour for LT AA2124 and LT AA6061. The delamination of the melted layer was observed for AA2124 but was not observed for AA6061 after exposure to 3.5% NaCl solution for 24 h. This was attributed to the formation of copper-rich segregation bands in the melted layer of AA2124 due to higher content of copper in AA2124 than AA6061. A significant number of micro-pores were present in the melted layer for AA2124 treated with high number of laser pulses, leading to the decrease of the corrosion resistance.

• Periodical: Materials Science Forum (Volumes 794-796)
• Pages: 235-240
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.794-796.235
• Online since: June 2014
• Authors: Dai Shu Qian*, Zhu Liu
• Keywords: Aluminium Alloy, Corrosion, Laser Surface Melting

References

[1] Z. Szklarska-Smialowska, Pitting corrosion of aluminium, Corrosion Science 41 (1999) 1743-1767.

DOI: 10.1016/s0010-938x(99)00012-8

[2] A. Boag, A.E. Hughes, A.M. Glenn, T.H. Muster, D. McCulloch, Corrosion of AA2024-T3 Part I: Localised corrosion of isolated IM particles, Corrosion Science 53 (2011) 17-26.

DOI: 10.1016/j.corsci.2010.09.009

[3] F. Zeng, Z. Wei, J. Li, C. Li, X. Tan, Z. Zhang, Z. Zheng, Corrosion mechanism associated with Mg2Si and Si particles in Al−Mg−Si alloys, Trans. Nonferrous Met. Soc. China 21 (2011) 2559-2567.

DOI: 10.1016/s1003-6326(11)61092-3

[4] K.A. Yasakau, M.L. Zheludkevich, S.V. Lamaka, M.G.S. Ferreira, Role of intermetallic phases in localized corrosion of AA5083, Electrochimica Acta 52 (2007) 7651-7659.

DOI: 10.1016/j.electacta.2006.12.072

[5] A.E. Coy, F. Viejo, F.J. Garcia-Garcia, Z. Liu, P. Skeldon, G.E. Thompson, Effect of excimer laser surface melting on the microstructure and corrosion performance of the die cast AZ91D magnesium alloy, Corrosion Science 52 (2010) 387-397.

DOI: 10.1016/j.corsci.2009.09.025

[6] F. Viejo, A.E. Coy, F.J. Garcia-Garcia, Z. Liu, P. Skeldon, G.E. Thompson, Relationship between microstructure and corrosion performance of AA2050-T8 aluminium alloy after excimer laser surface melting, Corrosion Science 52 (2010) 2179-2187.

DOI: 10.1016/j.corsci.2010.03.003

[7] T.M. Yue, L.J. Yan, C.P. Chan, C.F. Dong, H.C. Man, G.K.H. Pang, Excimer laser surface treatment of aluminum alloy AA7075 to improve corrosion resistance, Surface and Coatings Technology 179 (2004) 158-164.

DOI: 10.1016/s0257-8972(03)00850-8

[8] C. Kim, L.S. Weinman, Porosity formation in laser surface melted aluminium alloys, Scripta Metallurgica 12 (1978) 57-60.

DOI: 10.1016/0036-9748(78)90227-2

[9] F. Viejo, Z. Aburas, A.E. Coy, F.J. Garcia-Garcia, Z. Liu, P. Skeldon, G.E. Thompson, Performance of Al alloys following excimer LSM-anodising approaches, Surf. Interface Anal. 42 (2010) 252-257.

DOI: 10.1002/sia.3144

[10] Y. Yuan, Z. Aburas, T, Hashimoto, Z. Liu, P. Skeldon, G.E. Thompson, Microstructure Analysis and Corrosion Study of Excimer Laser Modified AA2024-T351 Aluminium Alloy, ECS Transactions 11 (15) (2008) 49-58.

DOI: 10.1149/1.2899047

[11] C. Padovani, A.J. Davenport, B.J. Connolly, S.W. Williams, E. Siggs, A. Groso, M. Stampanoni, Corrosion protection of AA2024-T351 friction stir welds by laser surface melting with Excimer laser, Corrosion Engineering, Science and Technology 47 (2012).

DOI: 10.1179/1743278211y.0000000020