Influence of Compaction Pressure on Magnetic Properties of Sendust Powder Core

Abstract:

Toroid-shaped soft magnetic powder cores (SMCs) were produced by cold pressing of the commercial sendust alloy powders. The characteristics of the commercial sendust alloy powder and the effect of compaction pressure on the magnetic properties, i.e., effective permeability μe, quality factor Q, DC-bias properties and volume power loss of sendust alloy powder cores were investigated. The results showed that the sendust alloy powder core with shaping pressure of 1932 MPa, annealing temperature of 953 K for 1 h and dielectric content of 0.96% presents the optimum magnetic properties with an effective permeability of 90, a total loss of 386 mW/cm3 at f=50 kHz and Bm=0.1 T, a DC-bias property of 64% at H=50 Oe.

• Periodical: Materials Science Forum (Volume 852)
• Pages: 79-83
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.852.79
• Online since: April 2016
• Authors: Ru Wu Wang, Feng Quan Zhang, Ding Wei, Ze Min Fang, Chun Zeng, Zhong Han Luo
• Keywords: Compaction Pressure, Magnetic Properties, Sendust Alloy, Soft Magnetic Powder Core

References

[1] Tajima S, Hattori T, Kondon M, Kishimoto H, Sugiyama M and Kikko T: 2005 IEEE Trans. Magn. 41 (10) 3280.

[2] Taghvaei A H, Shokrollahi H and Janghorban K: 2009 J. Magn. Magn. Mater. 321 (23) 3926.

[3] Shokrollahi H and Janghorban K: 2007 J. Mater. Process. Technol. 189 1.

[4] Yanagimoto K, Majima K, Sunada S and Aikawa Y: 2004 IEEE Transactions on Magnetics 40 (3) 1691.

[5] Takahashi M, Nishimaki S and Wakiyama T: 1987 J. Magn. Magn. Mater. 66 55.

[6] Kishimoto Y, Yamashita O and Makita K: 2003 Journal of Materials Science 38 3479.

[7] Retallick W B, Brady M P and Humphrey D L: 1998 Intermetallics 6 335.

[8] Say M G: Magnetic alloys and Ferrites, George Newnes Limited, London, 1954, P159.