Crystallization of Amorphous Cu49.7Ti31.8Zr11.3Ni7.2 Alloy

Article Preview

Abstract:

Bulk metallic glasses are attractive materials for structural and functional applications when compared to crystalline materials. The Cu-based glasses exhibit particular interest due primarily to their relatively low cost and high fracture resistance. In this work the Cu49.7Ti31.8Zr11.3Ni7.2 alloy was prepared from the mixture of pure metals by arc melting and following the ingot was re-melted by centrifugal casting in wedge-section copper mould. The structure of wedge bulk sample was evaluated by a combination of X-Ray Diffraction (XRD) and Differential Scanning Calorimetry (DSC). The results show that the amorphous state is formed in the thinner region and it is maintained up to thickness of 3.5 mm in the wedge bulk-sample. The crystallization temperature was observed above 400 °C coinciding with the studies of thermal crystallization by XRD and DSC. Dynamical heating of the amorphous phase from room temperature up to 750°C showed the formation of CuTi, Cu10Zr7 e Cu2TiZr crystalline phases.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

464-469

Citation:

Online since:

August 2016

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2016 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

[1] W. L. Johnson: Materails Research Society BulletinVol. 24 (1999), p.42.

Google Scholar

[2] A. Inoue: Acta Materiala Vol. 48 (2000), p.279.

Google Scholar

[3] T. Zhang, A. Inoue, T. Masumoto: Materials Transaction Vol. 32 (1991), p.1005.

Google Scholar

[4] J.K. Lee, S.H. Kim, W.T. Kim, D.H. Kim: Metals and Materials Intern. Vol. 7 (2001), p.187.

Google Scholar

[5] J.K. Lee, D.H. Bae, S. Yi, W.T. Kim and D.H. Kim: J. Non-Cryst. Solids Vol. 333 (2004), p.212.

Google Scholar

[6] A. Inoue, K. Amiya, I. Yoshii, N. Nishiyama and T. Masumoto: Mater. Sci. Eng. A Vols. 179/180 (1994), p.692.

Google Scholar

[7] H. Men and D.H. Kim: J. Mater. Res. Vol. 18 (2003), p.1502.

Google Scholar

[8] P. Wesseling, T.G. Nieh, W.H. Wang and J.J. Lewandowski; Scripta Mater Vol. 51 (2) (2004), p.151.

Google Scholar

[9] H. Choi-Yim, R. Busch and W. L. Johnson: J. Appl. Phys. Vol. 83 (1998), p.7993.

Google Scholar

[10] H.E. Kissinger: Analytical Chemistry Vol. 29 (1957), p.1702.

Google Scholar

[11] F.Q. Guo, S.J. Poon, G.J. Shiglet: Materials Science Forum Vols. 331–337 (2000), p.31.

Google Scholar

[12] ASM handbook, Alloy Phase Diagrams, 10th Ed., ASM International, Materials Park, Ohio, Vol. 3 (1992), p.512.

Google Scholar

[13] A. Takeguchi, A. Inoue: Materials Transaction Vol. 46 (12) (2005), p.2817.

Google Scholar

[14] R. Arroyave, T.W. Eagar, L. Kaufman: J. Alloys Compds Vol. 351 (2003), p.158.

Google Scholar

[15] E.S. Park, M.Y. Huh, J.H. Lee, H.J. Kim, J.C. Bae: Rev. Adv. Mater. Sci. Vol. 18 (2008), p.77.

Google Scholar

[16] L.C. Zhang, M. Calin, M. Adam, J, Eckert: Rev. Adv. Mater. Sci. Vol. 18 (2008), p.429.

Google Scholar