The Characteristic of Surface Layers on Austenitic Stainless Steel after Glow-Discharge Nitriding Process

Artur Sitko; Marek Szkodo; Maria Gazda

doi:10.4028/www.scientific.net/SSP.165.165

Paper Titles

Mechanical and Physicochemical Properties of Some Originally Made Composite Materials for Dental Fillings
p.142

Surface Activity and Fluid Sorption of Titanium Alloys Soaked in SBF Solution
p.147

Steel Strips Flattening in Ball Rolling Mill
p.153

Polymer-Surface Modification with a-C:N:H Layers Plasma Chemically Deposited in RF CVD and MW CVD Systems
p.159

The Characteristic of Surface Layers on Austenitic Stainless Steel after Glow-Discharge Nitriding Process
p.165

The Effect of Fabrication Method of Cobalt Base Clad Layer on Air Oxidation
p.169

Cobalt Base Clad Layer Resistance on the Corrosion under Low Sulfur Pressure
p.173

The Influence of Plastic Strain on the Corrosive Properties of Plasma Sprayed Intermetallic NiAl and Ni₃Al Coatings
p.177

The High Cyclic Failure Analysis of Welded Joints of CT Specimens
p.183

HomeSolid State PhenomenaSolid State Phenomena Vol. 165The Characteristic of Surface Layers on Austenitic...

The Characteristic of Surface Layers on Austenitic Stainless Steel after Glow-Discharge Nitriding Process

Abstract:

This paper presents investigation of surface layers. The diffusion layers were produced by using different parameters of reactive atmosphere (N2:H2). The research of the surface layers was performed using scanning electron microscope (SEM). The results of energy dispersive X-ray (EDX) analysis and X-ray diffraction (XRD) analysis are presented. Research reveals the influence of chemical constitution of reactive atmosphere on the change of properties of nitrided layers.