Utilization of Fly Ash in the Synthesis of Refractory Forsterite-Spinel Ceramics

Abstract:

Forsterite refractory ceramics is utilized in the metallurgical and cement industries as a lining of metallurgical furnaces and rotary kilns for its high refractoriness up to 1850°C and refractoriness under load above 1600°C. Another significant property of forsterite is its coefficient of linear thermal expansion utilized in the electrotechnical industry for ceramic-metal joints. Addition of aluminium oxide into the raw material mixture results in creation of magnesium-alumina spinel (MgO·Al₂O₃) which improves sintering, thermal shock resistance and mechanical properties in comparison with pure forsterite ceramics. Inexpensive source of aluminium oxide is fly ash. Utilization of fly ash, secondary energetic product of coal-burning power plants, is important for the environment and sustainable development. This paper evaluated properties of fly ash-based forsterite-spinel ceramics in comparison with alumina-based forsterite-spinel ceramics. Forsterite-spinel ceramics was synthesized from olivine, calcined magnesite and fly ash/alumina powders. XRD analysis was used to determine mineralogical composition, thermal analyses were used to determine the behaviour during firing and scanning electron microscopy to determine the morphology of crystal phases. Refractoriness of pyrometric cones, refractoriness under load, thermal shock resistance, coefficient of linear thermal expansion, water absorption, porosity and modulus of rupture were also determined on fired test samples.

• Periodical: Solid State Phenomena (Volume 321)
• Pages: 131-140
• DOI: https://doi.org/10.4028/www.scientific.net/SSP.321.131
• Online since: July 2021
• Authors: Martin Nguyen*, Radomír Sokolař
• Keywords: Alumina, Fly Ash, Forsterite, Refractory Ceramics, Spinel, Synthesis

References

[1] P. P. Budnikov, Technology of ceramics and refractories, MIT press Ltd, Cambridge, 1964, ISBN: 9780262523776, pp.270-283.

[2] W. Kingery, Introduction to ceramics, Wiley, New York, 1960, pp.261-284.

[3] F. Zhao, L. Zhang, Z. Ren, J. Gao, X. Chen, X. Liu and T. Ge, A novel and green preparation of porous forsterite ceramics with excellent thermal isolation properties, Ceramics International 45(3), 2019, pp.2953-2961,.

DOI: 10.1016/j.ceramint.2018.09.296

[4] M. Bouhifd, D. Andrault, G. Fiquet and P. Richet, Thermal expansion of forsterite up to the melting point, Geophysical research letters 23(10), 1996, p.1143–1146.

DOI: 10.1029/96gl01118

[5] Braulio, M.A.L., M. Rigaud, A. Buhr, C. Parr a V.C. Pandolfelli. Spinel-containing alumina-based refractory castables, Ceramics International 37(6), pp.1705-1724, 2011,.

DOI: 10.1016/j.ceramint.2011.03.049

[6] E. Mustafa, N. Khalil and A. Gamal, Sintering and microstructure of spinel–forsterite bodies, Ceram. Int. 28(6), 2002, p.663–667,.

DOI: 10.1016/s0272-8842(02)00025-1

[7] I. Ganesh, A Review on Magnesium Aluminate (MgAl2O4) Spinel: Synthesis, Processing and Applications, International Materials Reviews, 58(2), 2013, pp.63-112,.

DOI: 10.1179/1743280412y.0000000001

[8] R. B. Graf, F. M. Wahl and R. E. Grim, Phase transformations in silica-alumina-magnesia mixtures as examined by continuous x-ray diffraction: II. Spinel-silica compositions, The American mineralogist 48(1-2), 1963, pp.150-158.

[9] Y. Dong, S. Hampshire, J. Zhou, Z. Ji, J. Wang and G. Meng, Sintering and characterization of fly ash-based mullite with MgO addition, Journal of the European Ceramic Society 31,2011, p.687–695,.

DOI: 10.1016/j.jeurceramsoc.2010.12.012

[10] M. S. Kumar, M. Vanmathi, G. Senguttuvan, R. V. Mangalaraja and G. Sakthivel, Fly Ash Constituent-Silica and Alumina Role in the Synthesis and Characterization of Cordierite Based Ceramics, Silicon, 2018, pp.1-13,.

DOI: 10.1007/s12633-018-0049-0

[11] E. M. M. Ewais, A. A. M. El-Amir, D. H. A. Besisa, M. Esmat and B. E.H. El-Anadouli, Synthesis of nanocrystalline MgO/MgAl2O4 spinel powders from industrial wastes, Journal of Alloys and Compounds 691, 2017, pp.822-833,.

DOI: 10.1016/j.jallcom.2016.08.279

[12] W. Wons, K. Rzepa, M. Reben, P. Murzyn, M. Sitarz and Z. Olejniczak, Effect of thermal processing on the structural characteristics of fly ashes, Journal of Molecular Structure 1165, 2018, pp.299-304,.

DOI: 10.1016/j.molstruc.2018.04.008

[13] M. Nguyen and R. Sokolář, Influence of Fly Ash Addition in the Raw Mixture on Synthesis and Properties of Forsterite", Solid State Phenomena 296, 2019, pp.180-185,.

DOI: 10.4028/www.scientific.net/ssp.296.180

[14] M. Nguyen and R. Sokolář, Presence of magnesium-alumina spinel in forsterite ceramics and its influence during sintering and on resulting properties of fired body, IOP Conf. Ser.: Mater. Sci. Eng. 549(012025), 2019,.

DOI: 10.1088/1757-899x/549/1/012025

[15] M. Nguyen and R. Sokolář, Formation and influence of magnesium-alumina spinel on properties of refractory forsterite-spinel ceramics, Materiali in Tehnologije 54(1), 2020, pp.89-95,.

DOI: 10.17222/mit.2019.198