Effect of Mn Addition on Microstructure, Mechanical Properties and Die Soldering of Rheocasting Al-7Si-0.3Mg Alloys

Abstract:

The effect of Mn additions (up to 0.8 wt.%) into Al-7Si-0.3Mg alloy on the microstructure, mechanical properties and die soldering was firstly investigated in gravity die casting conditions, with the aim to obtain an optimized Mn addition level. Especially, the stirring testing on H13 die material was used to elucidate the effect of Mn additions on the Fe concentration in the Al melting as a function of melting temperature (690 °C) and holding time (up to 32 h), which can provide an indirect sign of die soldering. On this basis, the addition of 0.6wt.%Mn into Al-7Si-0.3Mg alloy was found to be beneficial for microstructure, strength and die soldering. Secondly, rheocasting of Al-7Si-0.3Mg alloy without (Mn-free alloy) and with 0.6 wt.% Mn (Mn-containing alloy) was performed. The addition of 0.6wt.%Mn into Al-7Si-0.3Mg alloy was found to have following effects: (i) solidification temperature of α-Al is increased and a higher (about 20 °C) rheocasting temperature is therefore needed, but no significant die soldering problem was observed even with increasing casting temperature, (ii) Mn-containing phase forms along grain boundaries and within Al matrix, which increases tensile and yield strength but decreases elongation in as-cast, T5 and T6 conditions, (iii) number density and volume fraction of pores increases, and (iv) die soldering slightly improves. This paper demonstrates that the addition of 0.6wt.%Mn into Al-7Si-0.3Mg alloy is beneficial for microstructure, strength and die soldering in both gravity die casting and rheocasting conditions.

• Periodical: Solid State Phenomena (Volume 347)
• Pages: 67-73
• DOI: https://doi.org/10.4028/p-U4O8Pv
• Online since: August 2023
• Authors: Jie Hua Li*, Ivo Spacil, Johannes Winklhofer, Fabian Hofstätter, Stefan Griesebner
• Keywords: Al-Si-Mg Alloy, Die Soldering, Mechanical Properties, Microstructure, Mn Addition, Rheocasting, Semi-Solid Process

References

[1] S.P. Midson, Semisolid Metal Casting. In ASM Handbook Aluminum Science and Technology; ASM: Almere, The Netherlands, 2018; Volume 2A, p.400–408.

DOI: 10.31399/asm.hb.v02a.a0006498

[2] Q. Han, S. Viswanathan, Analysis of the mechanism of die soldering in aluminum die casting, Metallurgical and materials transactions A. 33 (2002) 1-8.

[3] T. Bogdanoff, A.K. Dahle, S. Seifeddine, Effect of Co and Ni addition on the microstructure and mechanical properties at room and elevated temperature of an Al–7%Si alloy, International Journal of Metalcasting. 13 (2018) 434-440.

DOI: 10.1007/s40962-017-0178-z

[4] T. Bogdanoff, Development of aluminium-silicon alloys with improved properties at elevated temperature, Master thesis in Jönköping University, Sweden, 2017.

[5] A.S. Sani, I. Aliyu, E. Polycarp, Effect of chromium and cobalt additions on the corrosion resistance of aluminium-silicon-iron alloy, International Journal of Scientific & Engineering Research. 3 (2012) 1-10.