Failure Analysis on Tube Socket Crack of Supercritical Boiler Water Wall Header

Xiang Feng Zheng; Yun Jian Jiang; Yan Ting Feng; Qing Wang; Xiao Guang Niu; Xiao Jun Hao; Wen Bin Li; Zhong Wei Li; Xue Xia Xu; Wen Peng Li

doi:10.4028/www.scientific.net/AMM.204-208.4616

Paper Titles

The Numerical Research of Two-Degrees-of-Freedom Vortex-Induced Vibrations of Circular Cylinders
p.4598

Experimental Investigation on Tensile Mechanical Properties of CFRP-PCPs Composite Rebars
p.4602

Experimental Study on Mechanics Properties of CFRP-PCPs Composite Rebars under Uniaxial Load
p.4606

Conceptual Design and Hydrodynamic Analysis of a High-Speed Deformable Trimaran
p.4610

Failure Analysis on Tube Socket Crack of Supercritical Boiler Water Wall Header
p.4616

Experimental Studies on the Effects of Nozzle Structures on Characteristics of Submerged Gas Jet Noise
p.4620

Numerical Analysis of Variation Law about Vertical Additional Force of Monolayer Shaft Lining
p.4624

The Application of Pseudolinear Equivalent System in the Deformation Analysis of RC Structure Members
p.4629

Analysis of Four Finite Volume Schemes for Plane Stress Problems
p.4635

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vols. 204-208Failure Analysis on Tube Socket Crack of...

Failure Analysis on Tube Socket Crack of Supercritical Boiler Water Wall Header

Abstract:

Through methods, such as microscope analysis, mechanical analysis, chemical analysis, metallography examination and scanning electron microscope etc, the causes resulting in lots of tube socket cracks of supercritical boiler water wall header (15CrMo) have been analyzed. The result indicates failure of the supercritical boiler water wall header tube sockets are the ductile fracture and belong to thermal stress crack. The unreasonable structure, excessive thermal stress between header and sockets are the primarily inducement of crack failure.