Mixing Study of Aluminium Waste as Metal Powder for Waste Polystyrene Binder System in Metal Injection Molding (MIM)

Abstract:

The mixing process of a newly developed binder system based on waste polystyrene (PS) and palm kernel oil (PKO) to produce feedstock for metal injection molding (MIM) using aluminium waste as metal powder is described. Since mixing is a critical step in MIM process, therefore the mixture of powder and binder should be homogeneous and moldable. In this study, aluminium powder produced from waste aluminium alloy was mixed with a new binder system consisting of waste polystyrene and palm kernel oil in a Brabender Plastograph EC rotary mixer. Several tests were performed to assess the homogeneity of the feedstock that was produced at 60 vol.% powder loadings. The tests conducted were density, binder burn-out and SEM morphology observation. It was found that the feedstock shows good homogeneity and suitable for further processing in MIM.

• Periodical: Applied Mechanics and Materials (Volume 660)
• Pages: 239-243
• DOI: https://doi.org/10.4028/www.scientific.net/AMM.660.239
• Online since: October 2014
• Authors: Rosli Asmawi*, Mohd Halim Irwan Ibrahim, Azriszul Mohd Amin, Najwa Mustafa, N. Alawi
• Keywords: Aluminium Waste, Metal Injection Molding (MIM), Mixing

References

[1] Gokçe, A., and F. Findik. Mechanical and Physical Properties of Sintered Aluminum Powders., Journal of Achievements in Materials and Manufacturing Engineering, 30 (2008): 157-164.

[2] Hunt, W. H. New Directions in Aluminum-Based P/M Materials for Automotive Applications., International Journal of Powder Metallurgy 36 (2000): 50-56.

[3] Schaffer, G. B., T. B. Sercombe, and R. N. Lumley. Liquid Phase Sintering of Aluminum Alloys., Materials Chemistry and Physics 67 (2001): 85-91.

DOI: 10.1016/s0254-0584(00)00424-7

[4] R. Asmawi, M. H. I. Ibrahim, and A. M. Amin, Mixing and characterisation of stainless steel 316L feedstock for waste polystyrene binder system in metal injection molding ( MIM ), vol. 607, p.83–86, (2014).

DOI: 10.4028/www.scientific.net/amm.607.83

[5] R. Supati, N. H. Loh, K. A. Khor, and S. B. Tor, Mixing and characterization of feedstock for powder injection molding, no. November, p.0–5, (2000).

DOI: 10.1016/s0167-577x(00)00151-8

[6] L. Liu, N. H. Loh, B. Y. Tay, S. B. Tor, Y. Murakoshi, and R. Maeda, Mixing and characterisation of 316L stainless steel feedstock for micro powder injection molding, Mater. Charact., vol. 54, no. 3, p.230–238, Mar. (2005).

DOI: 10.1016/j.matchar.2004.11.014

[7] X. Kong, T. Barriere, and J. C. Gelin, Journal of Materials Processing Technology Determination of critical and optimal powder loadings for 316L fine stainless steel feedstocks for micro-powder injection molding, J. Mater. Process. Tech., vol. 212, no. 11, p.2173–2182, (2012).

DOI: 10.1016/j.jmatprotec.2012.05.023

[8] D. Checot-Moinard, C. Rigollet, and P. Lourdin, Powder injection moulding PIM of feedstock based on hydrosoluble binder and submicronic powder to manufacture parts having micro-details, Powder Technol., vol. 208, no. 2, p.472–479, (2011).

DOI: 10.1016/j.powtec.2010.08.045