The Preparation Process and Mechanism of the Iron-Red Fancy Glaze under High Temperature Reducing Atmosphere

Xiao Tao Shi; Ting Zhang

doi:10.4028/www.scientific.net/AMM.670-671.318

Paper Titles

Research of Aluminosilicate Refractorial Erosion Process on the HCL in Blast Furnace Gas
p.300

Dyeing of Bamboo Viscose Fiber with Gardenia Yellow and Sodium Copper Chlorophyll
p.305

The Effect Nucleating Agent on Open-Celled Morphology of Polymer in Vibration
p.309

Technical Research for Oil Well Variable Frequency Electromagnetic Field Paraffin Prevention
p.313

The Preparation Process and Mechanism of the Iron-Red Fancy Glaze under High Temperature Reducing Atmosphere
p.318

Large-Scale Growth of Nitrogen-Doped via Solvothermal Synthesis
p.323

Application of Organosilicone and Gyoxal Crosslinking Agents on Tussah Silk Fabric
p.327

Effects of High Added Quantity SSA-SSP-GSP on Resistance to Carbonation of Concrete
p.333

Evaluation the Strength of Cement Systems, Modified by Accelerators
p.339

HomeApplied Mechanics and MaterialsApplied Mechanics and Materials Vols. 670-671The Preparation Process and Mechanism of the...

The Preparation Process and Mechanism of the Iron-Red Fancy Glaze under High Temperature Reducing Atmosphere

Abstract:

Based on the research of the split-phase glaze in the CaO-SiO₂-P₂O₅ series ,this thesis analyzes and discusses the effects of glaze’s formula and firing condition on the making of iron-red fancy glaze, and then comes to an scientific way to make bright-coloured iron-red fancy glaze with homogeneously-distributed crystalline under a wide range of temperature.