The Effect of Polymer Emulsion Addition on the Setting Time, Crack Formation and Strength of Cementitious Patch Repair Mortars

Abstract:

With millions of square meters of ageing exposed concrete surfaces throughout the world, concrete patch repair is becoming a major component of the civil construction industry. To ensure effective and efficient repairs and rehabilitation of deteriorating concrete surfaces, patch materials with excellent workability during the repair phase and durability during its design life cycle are required. The addition of polymer emulsions to cementitious repair mortars increase the setting time, crack resistance while negatively affects the strength properties of the mortar. Polymer emulsions include natural rubber, polyacrylonitrile and polivinylacetate, to name just a few [1]. This paper focus on the effect of adding different polymer emulsions at varying dosages to cementitious repair mortars to obtain a better understanding of the influences on setting times, crack formation properties and curing regime requirements for optimal strength development. Ambient temperature and relative humidity were kept constant during the testing cycles. The results obtained indicated that the introduction of a polymer emulsion tend to reduce both the initial and final setting times of the repair mortars but that is extends the duration between initial and final set when compared to unmodified repair mortars. Compressive strength reductions were observed when adding polymer emulsions to the repair mortar but it was clear that crack formation was eliminated with the addition of the emulsions

• Periodical: Advanced Materials Research (Volume 1129)
• Pages: 86-93
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.1129.86
• Online since: November 2015
• Authors: Deon Kruger*, Neil Herbst, Jannes Bester
• Keywords: Compressive Strength, Crack Formation, Patch Repair Mortar, Polymer Emulsion, Setting Time

References

[1] M. Miller, (2005), Polymers in cementitious materials, Shropshire, United Kingdom, Rapra Technology Limited.

[2] B. Addis, (2004), Fundamentals of concrete, Cement and Concrete Institute. Midrand, South Africa.

[3] Y. Ohama, (1995), Handbook of polymer-modified concrete and mortars: properties and process technology. New Jersey, Noyes Publications.

[4] W. O. Nutt, T. A. Downing, J. A. Forrester, A. C. Griffiths, P. R. Hills, M. Levitt, A. J. Majumdar, D. A. Smith, R. N. Swamy, (1975).

[5] Product information for operation of Vicatronic Apparatus (2009), Available from: http: /www. matest. com.

[6] SANS 50196-3: 2006 – Methods of testing cement, Part 3: Determination of setting times and soundness. South African Bureau for Standards, South Africa.

[7] SANS 5863: 2006 Concrete tests – Compressive strength of hardened concrete. South African Bureau for Standards, South Africa.

[8] SANS 6255: 2006 Mortar tests – Compressive strength of mortar. South African Bureau for Standards, South Africa.

[9] SANS 50196-1: 2006 Methods of testing cement – Part 1: Determination of strength. South African Bureau for Standards, South Africa.

[10] B. H. Ahmadi, (2000), Initial and final setting time of concrete in hot weather. Materials and Structures, 33 (8), October, pp.511-514.

DOI: 10.1007/bf02480528

[11] N. Delatte, (2009), Failure, distress and repair of concrete structures, Elsevier, United Kingdom.