Study on Debonding Failure Behavior of RC Beams Combination Strengthened with Carbon Fiber Reinforced Polymer and Steel Plates

Abstract:

In order to investigate the debonding failure mechanism,the distributions of interfacial shear stress between cracks and the influence of preload of on the ultimate load and interfacial shear stress,one reference beam and five beams strengthened with CFRP and steel plate at different level of perload were tested and analyzed.The experimental result indicated that the perload level has less influence on the ultimate capacity.Moreover,when debonding failure of sheet-end interface of concrete beams strengthened with CFRP and steel plate is avoided,the debonding failure of reinforced beams at perload level will occur in the position of midspan.At last,on the basis of cross-sectional equilibrium and compatiable conditions,an analytical model of interfacial bond shear stress is obtained, meanwhile the analytic model favorably matched with the experimental results.

• Periodical: Advanced Materials Research (Volumes 243-249)
• Pages: 597-609
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.243-249.597
• Online since: May 2011
• Authors: Xu Yu Xiong, Hai Feng Xu
• Keywords: Carbon Fiber (CF), Combination Strengthening, Crack, Debonding Failure, Interfacial Shear Stress, Steel Plate

References

[1] Xiong Xueyu,Xu Haifeng. Experimental research and parametric analysis on flexural performance of reinforced concrete beams combination strengthened with bonded CFRP and steel plates under sustaining load [J]. Building Structure，2010: 40(5):37-41.(in chinese)

[2] Xiong Xueyu,Xu Haifeng. Reserach on RC beams combination strengthened with carbon fiber reinforced polymer and steel plates under sustaining load [J]. Industrial Construction，2010: 40(4):131-136. (in chinese)

[3] LU Yiyan,ZHOU Ting. Experimental Research on Flexural Performance of Reinforced Concrete Beams Combination Strengthened with Bonded Carbon Fiber Reinforced Polymer and Steel Plates[J]. Journal of the Railway Society，2006:28(1):80-87. (in chinese)

DOI: 10.14359/51728064

[4] LU Yiyan,ZHOU Ting. Ddbonding Failure of Beams Combined Strengthened with CFRP and Steel Plate[J]. Chinese Journal of Applied Mechanics，2006: 23(2):284-288. (in chinese)

[5] Lin Xinyan,Cao Shuangyin. Study on bond behavior of inter-crack CFRP and concrete in beams strengthened with fibers [J].Engineering Mechanics，2008: 25(11):149-155. (in chinese)

[6] Li Songhui,Zhao Guofan,Wang Songgen. Mechanism of cover delamination or FRP debonding of CFRP strengthened RC beams at different stage[J]. Engineering Mechanics，2005: 22(1):153-158. (in chinese)

[7] Yao Jian,Teng Jinguang. Plate end debonding failure loads of FRP or steel plated RC beams[J]. Acta Materiae Compositae Sinica，2005: 22(1):153-158.

[8] Li Yan,Pan Jinglong. Experimental research on debonding failure of plate-end of RC beam strengthened with CFRP[J]. Journal of HARBIN Institute of Technology，2005: 37(5):687-693. (in chinese)

[9] S.T. Smith J.G. Teng. FRP-strengthened RC beamsⅡ:Assesment of debonding strength models[J].Engineering Structures, 2000, 24:397-417．

DOI: 10.1016/s0141-0296(01)00106-7

[10] G.Monti,E,Spacone. Reinforced concrete fiber beam with bond-slip[J].ASCE Journal of Sturctural Engineering, 2000, 126(6):654-661．

DOI: 10.1061/(asce)0733-9445(2000)126:6(654)

[11] E,Spacone,S.Limkatanyu. Responses of reinforced concrete members including bond-slip effects[J].ACI Sturctural Journal, 2000,97(6):831-839．

DOI: 10.14359/9628

[12] A.Aprile,E,Spacone. Role of bond in RC beams strengthened with steel and FRP plates[J].ASCE Journal of Sturctural Engineering, 2001, 127(12):1445-1452

DOI: 10.1061/(asce)0733-9445(2001)127:12(1445)

[13] Yang Yongxing,Yue Qingrui,Ye Lieping. Calculation for Flexural Debonding Bearing Capacity of RC Beams Strengthened with Carbon Fiber Sheets [J].China Civil Engineering Journal，2004: 37(2):23-32. (in chinese)

[14] Lu Xingzheng,Teng Jingguang,Ye Lieping. Finite element analysis of intermediate crack-induced debonding in FRP strengthened RC beams [J]. Engineering Mechanics，2004: 37(2):23-32. (in chinese)

DOI: 10.12989/sem.2015.56.3.473