Study on Preparation of NR/BR Table Tennis Bat Rubber

Abstract:

Table tennis bat rubber was prepared by using natural rubber (NR) and butadiene rubber (BR). The effects of the blending ratio of NR and BR, contents of accelerator and sulfur on the performance of rubber racket were studied. The results showed that when under conditions of 160°C, 10min and 15MPa in the curing press, total amount of material is 100 phr .Including the NR/BR ratio was 0.65/0.35 (wt), the content was 90 phr the accelerator of DM/D ratio was 0.382/0.618, the content was 2.5 phr and the content of sulfur was 2.5 phr, the compound had a high vulcanization rate, an excellent physical and mechanical properties and aging performance.

• Periodical: Advanced Materials Research (Volumes 311-313)
• Pages: 1173-1176
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.311-313.1173
• Online since: August 2011
• Authors: Hong Long Xing, Qi Yu Tao
• Keywords: Accelerant, Blending Ratio, Butadiene Rubber, Natural Rubber (NR), Sulfur, Table Tennis Bat

References

[1] Rob N. Mangnus: Kaut schuk Gummi Kunst stoffe, Vol. 56 (2003), p.322.

[2] M. Abdul Kader, Anil K1Bhowmick: Polymer Degradation and Stability(2003), p.283.

[3] Joaehim Zeeh, Gunther Lechner, U.S. Patent 6,335,413.(2002)

[4] Haizhen Luo:Tropical Agriculture Engineering (2006), p.29, In Chinese.

[5] Wanlan Jiang: World Rubber Industry Vol. 36(2009), p.11, In Chinese.

[6] WU Weili,CHEN Dajun: Journal of Applied Polymer Science Vol. 101(2006), p.4462.

[7] Zhang Yuanxi, Zhou Liling: China rubber/plastics technology and equipment Vol. 27(2011), p.26, In Chinese.

[8] Hsien,Tang Chiu , PeirAn Tsai: Journal of Materials Engineering and Performance Vol. 15 (2006), p.88.

[9] Weixing, Yuchuan Xing:China Rubber Industry Vol. 54 (2007), p.668, In Chinese.

[10] Junyu Luo, Xingmei Yang:China rubber industry Vol. 1 (1998), p.17, In Chinese.

[11] G. K. Jana and C. K. Das.: Macromolecular Research Vol. 13 (2005) p.30.