600°C Isothermal Section of the Zn-Fe-Nb Ternary System at the Zn-Rich Corner

Abstract:

The isothermal section of the Fe-Zn-Nb ternary system at 600 oC was determined using the equilibrated alloys with the aid of diffusion couple approach. The specimens were investigated by means of SEM-EDS analysis, SEM-WDS analysis and X-ray diffraction. A true ternary phase T was identified, this phase is in equilibrium with ε, NbZn3, Γ, δ, and η - Zn phases respectively in the system. The solubility of Nb in η - Zn and δ phase is limited and that of Zn in ε is up to 10.0%.

• Periodical: Advanced Materials Research (Volumes 391-392)
• Pages: 1210-1214
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.391-392.1210
• Online since: December 2011
• Authors: Hao Tu, Xin Ming Wang, Ya Liu, Chang Jun Wu, Jian Hua Wang, Zhi Li, Xu Ping Su
• Keywords: Phase Diagram, Zinc Based Alloy, Zn-Fe-Nb

References

[1] Debanshu, Bhattacharya and C. Cheng: Galvatech 04 Conference Proceedings, (2004) p.509.

[2] C.E. Jordan and A.R. Marder: J. Mater. Sci. Vol. 32 (1997), p.5593.

[3] R.A. Marder, Prog: Mater. Sci. Vol. 45 (2000), p.191.

[4] G. Tither, I.C. Garcia, M. Hua and A.J. Deardo: ISIJ. (1994), p.293.

[5] Hao Tu, Xuping Su and Fucheng Yin et al: J. Alloys Compd Vol. 485 (2001), p.270.

[6] X. Su, N.Y. Tang and J.M. Toguri: J. Alloys Compd. Vol. 325 (2001), p.129.

[7] J. NaKano, V.D. Malakhov and G.R. Purdy: Calphad. Vol. 29 (2005), p.276.

[8] W. Xiong, Y. Kong, Y. Du, Z.K. Liu, M. Selleby and W.H. Sun: Calphad. Vol. 1 (2009), p.2.

[9] C. Toffolon and C. Servant: Calphad. Vol. 24 (2000), p.97.

[10] Z. Moser: J. Phase Equilib. Vol. 13 (1992), p.425.

[11] N.Y. Tang, X. Su and J.M. Toguri: Calphad. Vol. 25 (2001), p.267.

[12] X. Su, N.Y. Tang and J.M. Toguri: Can. Metall. Q. Vol. 40 (2001), p.377.

[13] X.H. Tang, F.C. Yin, X.M. Wang, X. Su and N. Y Tang: J. Phase Equilib. Diff. Vol. 28 (2007), p.355.

[14] N.Y. Tang, X. Su and X. Yu: Metallkd. Vol. 94 (2003), p.116.