Performance of Anti-Erosion and Anti-Oxidation of High Al Steels at 1373K

Abstract:

The effect of Al content on the anti-erosion and anti-oxidation performance of high Al steels at 1373K is studied in this paper. By 168-hour heat treating at 1373 K and at oxidation atmosphere, These results show that for comparing non-Al steel and low-Al (w[Al]=1.14%) steel sample there are a more obvious and easily-dropping oxidation layer in surface in 24 h , the average oxidation rate is up to 0.406 mg/(cm2.h), but for high Al steel, there is a thinner gray oxidation layer in surface and a more fast oxidation rate for w[Al]<5% sample , and there is a thin, close and yellow gloss film and the average oxidation rate is only 0.016 mg/(cm2.h) for w[Al]=8.46% sample. The average erosion rate is 0.096 mg/cm2.h in initial 24 h and thereafter the erosion is very slow. But there is a higher erosion rate and the average erosion rate is 0.594 mg/(cm2.h) in 6 % HCl solution for high Al steel sample and comparing non-Al steel. Accordingly high Al steel possesses a good performance of high temperature anti-oxidation and anti-erosion in NaCl solution.

• Periodical: Advanced Materials Research (Volume 549)
• Pages: 679-682
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.549.679
• Online since: July 2012
• Authors: Hai Chuan Wang, Zhi You Liao, Shi Jun Wang, Yun Zhou, Yuan Chi Dong
• Keywords: Anti-Erosion, High Al Steel, High Temperature Anti-Oxidation, Performance

References

[1] Wu J Z , Yang H G , Process of Feeding Al in Wire in Mould of Slab Concaster[J], Special Steel, 2001, 22(6): 45~46 (in Chinese).

[2] Zhou Y, Wang S J, Wang H C, etc., Process of Feeding Al Wire in Slab Concasting Mould [J], Special Steel, 2003, 24(1): 39~41 (in Chinese).

[3] Cao X Z, Cheng A Y, Structure and Performance of Hot-Al Impregnation [J], PTCA(Part A: Physical Testing), 2002, 38(6): 240~242 (in Chinese).

[4] Ding Y, Huang X L, Gu B Q, Microstructure and Anti-oxidation Properties of Hot-Dip Aluminized Q235 Steel [J], Chemical Engineering & Machine, 2001, 28(4): 197~200 (in Chinese).

[5] Yu D Y, Luo Z Y, Li H F, etc., Corrosion Behavior of Al Hot Dipped Steel in H2S-3%NaCl- H2O System [J], Materials Protection, 2001, 34(6): 10~12 (in Chinese).