Preparation of Denatured Alcohol-Modified SPI-Based Adhesive

Yu Feng Ban; Hai Feng Zhu; Wei Zhao

doi:10.4028/www.scientific.net/AMR.557-559.987

Paper Titles

Research on the Influence of Stiffness of Copolymer(N-Tert-octylacrylamide/Acrylic acid/Methyl methacrylate/Butylaminoethyl Methacrylate/Hydroxypropyl Methacrylate) by Methyl Methacrylate and N-Tert-Octylacrylamide
p.968

Synthesis and Characterization of a Novel Linear Benzoxazine-Containing Polytriazole via Metal-Free Click Reaction and its Self-Crosslinking Behavior
p.973

Development of Outlast Fiber and Study about its Character of Thermoregulation
p.979

Actinozoan-Like Carbon Materials Prepared via a Solvothermal Route
p.983

Preparation of Denatured Alcohol-Modified SPI-Based Adhesive
p.987

Thermal Stability of a Novel Polytriazoleimide
p.991

Studied on Preparation Montmorillonite Modified by CTAMB and Adsorption Performance on Nitrobenzene
p.996

Preparation of Bone Glue Adhesives Using Epichlorohydrin Modification
p.1005

Rheological Properties and Microstructures of Thermo-Sensitive Microemulsion-Based Gels
p.1009

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 557-559Preparation of Denatured Alcohol-Modified...

Preparation of Denatured Alcohol-Modified SPI-Based Adhesive

Abstract:

An environment-friendly soy protein isolate (SPI)-based adhesive for wood was prepared using denatured alcohol-modified SPI, calcium hydroxide and sodium silicate. On the basis of the single factor test results, an orthogonal test of 4 elements and 3 levels was carried out to optimize formula ingredients. The modified SPI adhesive contained more calcium hydroxide than unmodified SPI adhesive and exhibited good performance. The shear strength of the specimen bonded with the modified adhesive was 82.3 MPa; after three cycles of water-soaking and air-drying, the decrease in shear strength was as low as 7.9%.