Experimental Study on Rutile TiO2 Surface Coated with Al2O3 and ZrO2

Zhi Qiang Luo; Xin Hong Chen; Li Li

doi:10.4028/www.scientific.net/AMR.581-582.387

Paper Titles

Effects of Nano-SiO₂ in Electrolytes on Surface Properties of Micro-Arc Oxidation Ceramic Coatings Formed on New Casting Aluminum Alloy
p.368

Effects of SiO₂ and Al₂O₃ Contents of Converter Slag on Metallurgical Properties
p.373

Electrical Discharge Machining of Nickel-Based Super Alloy
p.378

Electrochemical and Gaseous Hydrogen Storage Capacities of As-Spun Nanocrystalline and Amorphous Mg₂Ni_0.6M_0.4 (M=Cu, Co) Alloys
p.382

Experimental Study on Rutile TiO₂ Surface Coated with Al₂O₃ and ZrO₂
p.387

Fabrication of TiO₂ Nanotubes by Anodic Oxidation for the Dye Sensitized Solar Cell Application
p.391

Hydrothermal Synthesis of Mesoporous Al₂O₃: Influences of pH Values and Aluminum Precursors
p.396

Impact of H₃BO₃ on Foaming Action of CaCO₃in Borosilicate Foam Glasses
p.401

Impact of Melt Spinning on Electrochemical Hydrogen Storage Characteristics of Mg₂₀Ni₉M₁ (M=Cu, Co) Alloys
p.405

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 581-582Experimental Study on Rutile TiO2 Surface Coated...

Experimental Study on Rutile TiO₂ Surface Coated with Al₂O₃ and ZrO₂

Abstract:

The industrial test of rutile TiO2 surface coated with Al2O3 and ZrO2 was completed using the TiO2 coated technology of low viscosity process at the TiO2 factory of PanGang group. The viscosity during the coating process, sample elements and elements distribution were respectively measured by viscometer, XRF and EDS. The results show that the viscosity of coating process is obviously lower than viscosity of existing coating technology, sample element distribution is more uniform on TiO2 surface, and the deposition rate of coating reagent is higher than it of sample using existing coating technology. The Al2O3 content fluctuation value of sample and sample using existing coating technology is respectively 0.56%, 1.19% on sample surface different points, and the Al2O3 deposition rate is 93%, 84.17%, respectively.

You might also be interested in these eBooks

Frontiers of Materials, Chemical and Metallurgical Technologies

View Preview

Info:

Periodical:

Advanced Materials Research (Volumes 581-582)

Pages:

387-390

DOI:

https://doi.org/10.4028/www.scientific.net/AMR.581-582.387

Citation:

Cite this paper

Online since:

October 2012

Authors:

Zhi Qiang Luo, Xin Hong Chen, Li Li

Keywords:

Coating, Deposition Rate, TiO₂, Uniformity, Viscosity

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

References

[1] Z.N. Tang. Production and Environmental Treatment of Titanium Dioxide (Chem Ind Press, China, 2000), in Chinese.

Google Scholar

[2] Mattheew L. Taylor, Gayle E. Morris and Roger St. C. Smart: Journal of Colloid and interface Science, Vol. 262 (2003), pp.81-88.

Google Scholar

[3] K. Li, H. Liu, Y.L. Yu et. al: Chemical Research and Application, Vol. 19 (2007), pp.1250-1254, in Chinese.

Google Scholar

[4] A.L. Cui, T.J. Wang, Y. Jin et. al: Chemical Journal of Chinses Universities, Vol. 19 (1998), pp.1227-1729, in Chinese.

Google Scholar

[5] Q. Li, H. F, Hu, L.Y. Wu et. al: Iron Steel Vanadium Titanium, Vol. 25 (2004), pp.9-14, in Chinese.

Google Scholar

[6] K. Li, H. Liu, P. Zhang et. al: Inorganic Chemicals Industry, Vol. 40 (2008), pp.33-35, in Chinese.

Google Scholar

[7] A.L. Cui, T.J. Wang, Y. Jin et. al: Engineering Chemistry and Metallurgy, Vol. 20 (1999), pp.178-181, in Chinese.

Google Scholar

[8] C.L. Kang, C.Z. Li, Z. T, Wang et. al: Journal of East China University of Science and Thchnology, Vol. 27 (2001), P. 631-634, in Chinese.

Google Scholar

[9] Fotou G. P, Kodas T. T, Anderson B: Aerosol Science and Technology, Vol. 33 (2000), P. 557-571.

Google Scholar