Preparation of High-Temperature-Resistance Silicone Paints

Abstract:

Silicone paints were prepared by mixing as-synthesized silicone resin, pigments, fillers and other additives. The effects of the solvent, addition of pearlescent powder, addition of KH550, addition of butyl titanate and temperature on the performance of high-temperature-resistance silicon paints or coatings were studied. The results showed that the optimal coating was cured at room temperature and had no cracks after 10 times cold and hot alternation in the condition of 500oC~cold water. The pencil hardness and the adhesion of coating reached 3H and 1 level, respectively.

• Periodical: Advanced Materials Research (Volumes 602-604)
• Pages: 1676-1679
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.602-604.1676
• Online since: December 2012
• Authors: Guo Jun Li, Yan Bin Wei, Rui Ming Ren
• Keywords: Coating, High-Temperature Resistance, Room Temperature Curing, Silicone Resin

References

[1] S. Feng, J. Zhang and M. Jiang: Silicone Polymer and Its Application. Beijing: Chemical Industry Press, 2004, p.153. (In Chinese).

[2] Z. Wang, C. Hao, Q. Ma et al: Journal of Hangzhou Normal University Vol. 10(2011), p.511.

[3] S. Xing and Y. Wang: Synthesis Process and Product Application of Organic Silicon. Beijing Chemical Industry Press, 2000, p.717. (In Chinese).

[4] Q. Xu: China Paint 2 (1998), p.31. (In Chinese).

[5] D. Zheng: Printing Engineering Vol. 6(2003), p.26. (In Chinese).

[6] R. Zhou: Electroplating & Finishing Vol. 29(2010), p.51. (In Chinese).

[7] H. Wang, Y. Li, G. Gou et al: Journal of Beijing University of Chemical Technology Vol. 35(2005), p.17. (In Chinese).

[8] G. Li, B. Zhang and R. Ren: CN 101857674A [P], 10. (2010).

[9] B. Zhang, G. Li and R. Ren: Organic Silicone Materials Vol. 25(2011), p.18. (In Chinese).