Fabrication and Properties of Cu-Cr Coatings on the Inner Wall of Steel Pipe by Mechanical Alloying Method

Abstract:

The mechanical alloying method process has been innovatively used to prepare Cu-Cr coating on the inner wall of steel pipe. The effect of the rotating speed on thickness, microhardness and friction coefficient of the Cu-Cr coating was investigated. The coating thickness was measured from all samples using optical microscope. The microhardness was analyzed by Digital Microhardness Tester. The friction coefficient was tested by high speed reciprocating friction testing machine. The results show that the coating thickness is 26, 29 and 31μm at the rotating speed of 200, 250 and 300 rpm. The microhardness of the Cu-Cr coating prepared at 200, 250 and 300 rpm are about 760, 780 and 830 Hv. The friction coefficient of the Cu-Cr coating prepared at 200 rpm are about 0.25, 0.40 and 0.38 at the frequencies of 3, 4 and 5 Hz. The friction coefficient of the Cu-Cr coating prepared at 250 rpm are about 0.30, 0.29 and 0.20 at the frequencies of 3, 4 and 5 Hz. The friction coefficient of the Cu-Cr coating prepared at 300 rpm are about 0.10, 0.13 and 0.09 at the frequencies of 3, 4 and 5 Hz.

• Periodical: Advanced Materials Research (Volumes 602-604)
• Pages: 1663-1666
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.602-604.1663
• Online since: December 2012
• Authors: Zhong Qing Tian, Guo Xing Zhang, Wei Jiu Huang, Yu Kai Zhu
• Keywords: Mechanical Alloying, Microstructure, Surface Coating, Tribological Property

References

[1] L. Takacs, A.R. Torosyan: J. Alloys Compd. Vol. 434–435 (2007), p.686

[2] S. Romankov, S.V. Komarov, E. Vdovichenko, Y. Hayasaka, N. Hayashi, S.D. Kaloshkin, E. Kasai: Int. Journal of Refractory Metals & Hard Materials Vol.27 (2009), p.492

DOI: 10.1016/j.ijrmhm.2008.10.005

[3] S. Romankov, W. Sha, S. D. Kaloshkin, K. Kaevitser: Surf. Coat. Technol. Vol. 201 (2006), p.3235

[4] S. Romankova, Y. Hayasakab, I. V. Shchetininc, E. Kasaid, S. V. Komarove, J. M. Yoon: Materials Science and Engineering A Vol. 528 (2011),p.3455

[5] C. C. Wu, F. B. Wu: Surface & Coatings Technology Vol. 204 (2009), p.854

[6] R. Pouriamanesh, J. Vahdati-Khaki, Q. Mohammadi: Journal of Alloys and Compounds Vol. 488 (2009), p.430

DOI: 10.1016/j.jallcom.2009.08.150

[7] S. Romankov, S. D. Kaloshkin, Y. Hayasaka, N. Hayashi, E. Kasai, S. V. Komarov: Journal of Alloys and Compounds Vol. 484 (2009), p.665

DOI: 10.1016/j.jallcom.2009.05.016

[8] X. Yan, G. Xu: Materials Science and Engineering B Vol. 166 (2010), p.152

[9] K. Lu, J. Lu: J. Mater. Sci. Eng. A Vol. 375–377 (2004), p.38

[10] I. Farahbakhsha, A. Zakeria, P. Manikandan, K. Hokamoto: Applied Surface Science Vol. 257 (2011), p.2830

[11] A. Revesz, L. Takacs: J. Alloys Compd. Vol. 441 (2007), p.111