Interaction between the Dislocations and Precipitates in Fe-40Ni Alloy during Stress Relaxation

Article Preview

Abstract:

Transmission electron microscopy (TEM) was used to study the interaction between the dislocations and strain induced precipitates during relaxation process after deformation in Fe-40Ni alloy. The experimental results demonstrate that the dislocation density is very high and distribute randomly before relaxation. As the relaxation time increasing, dislocation walls will form gradually by polygonization. The strain induced precipitates retards their progress. In the final relaxation stage, most dislocations get rid of pinning of precipitates and the dislocation walls have developed into subgrains with large size.

You might also be interested in these eBooks

Info:

Periodical:

Pages:

137-140

Citation:

Online since:

February 2013

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2013 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] Zhenqiang, Wang, Xinping, Mao, Zhigang: Strain-induced precipitation in a Ti micro-alloyed HSLA steel Materials Science and Engineering A. Vol. 529 (2011), p.459.

DOI: 10.1016/j.msea.2011.09.062

Google Scholar

[2] Wang X M, He X L, Yang S W: Refining of intermediate transformation microstructure by relaxation processing. ISIJ International. Vol. 42 (12) (2002), p.1553.

DOI: 10.2355/isijinternational.42.1553

Google Scholar

[3] Shaoqiang Yuan, Shanwu Yang, Xuemin Wang: Over-relaxation effect of deformed austenite on ageing behavior of an Nb-bearing microalloyed steel. Journal of University of Science and Technology Beijing, Vol. 12(3) (2005), p.248.

Google Scholar

[4] M. Verdier, M. Janecek, Y. Brechet, P. Guyot: Microstructural evolution during recovery in Al-2. 5%Mg alloy. Materials Science and Engineering A, Vol. 248 (1988), P. 187.

DOI: 10.1016/s0921-5093(98)00488-2

Google Scholar

[5] Y. LAN, H.J. KLAAR, W. DAHL: Evolution of Dislocation Structures and Deformation Behavior of Iron at Different Temperatures: Part Ⅱ. Dislocation Density and Theoretical Analysis. METALLURGICAL TRANSACTIONS A, Vol. 23A (1992), p.545.

DOI: 10.1007/bf02801172

Google Scholar

[6] Yoshitaka Adachi: Nucleation of bcc phase from work-hardened fcc phase, [in] 6th workshop on the Ultra-steel. Tsukuba, 2002, p.91.

Google Scholar

[7] S.Q. Yuan, S.W. Yang, C.J. Shang: Strain Induced Precipitation in a Multi-Microalloyed Steel Containing Nb and Ti during RPC Processing. Materials Science Forum, Vol. 426-432(2003), p.1307.

DOI: 10.4028/www.scientific.net/msf.426-432.1307

Google Scholar

[8] Shaoqiang YUAN, Guoli LIANG, Xiaojuan ZHANG: Strain-Induced Precipitation in Nb-Bearing Low Carbon Multi-Microalloyed Steel. Advanced Materials Research, Vol. 97-101 (2010), p.560.

DOI: 10.4028/www.scientific.net/amr.97-101.560

Google Scholar

[9] Guoli Liang, Shaoqiang Yuan: Effect of Long Time Isothermal after Deformation on Tempering Microstructure and Nanometer Precipitation in Nb-bearing Micro-alloyed Steel. Journal of computational and theoretical Nanoscience, Vol. 9(2012), p.1325.

DOI: 10.1166/jctn.2012.2195

Google Scholar