Effects of T6 Age Hardening on Microstructure and Mechanical Properties of Al-Si-Cu Cast Aluminium Alloy

Abstract:

Effects of T6 artificial aging heat treatment on microstructure, microhardness and ultimate tensile strength of Al-4.93 wt% Si-3.47 wt% Cu alloy were investigated. The T6 age hardening treatment consists of solution treatment at 500±5°C for 8 hours followed by quenching into hot water at 80°C and artificial aging at 150, 170, 200 and 230°C for 1-48 hours followed by quenching into hot water. Microstructure was characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), and transmission electron microscopy (TEM). XRD and SEM revealed that the microstructure in the as-cast condition consists of primary dendritic α-Al, acicular-plate and globular forms of eutectic Si and intermetallic phases including globular Al₂Cu and a flake-shape Al₅FeSi. By T6 aging hardening, some intermetallics were dissolved and spheroidized. The volume fraction of eutectic phases in the as-cast, solution-treated, and solution-treated plus aging at 170°C for 24 hours is 17%, 12% and 10%, respectively. TEM results showed that precipitates in under-aging condition at 170° C for 6 hours are in the form of disc shape with the diameter in the range of 7-20 nm. At peak aging at 170°C for 24 hours, thin-plate precipitates with about 3-10 nm in thickness and 20-100 nm in length were found, lengthening to about 30-200 nm at longer aging time. The microhardness and ultimate tensile strength were increased from 71 HV0.05 and 227 MPa in the as-cast condition up to 140 HV0.05 and 400 MPa after solution treatment plus aging at 170°C for 24 hours, and decreased at prolong aging time.

• Periodical: Advanced Materials Research (Volume 770)
• Pages: 88-91
• DOI: https://doi.org/10.4028/www.scientific.net/AMR.770.88
• Online since: September 2013
• Authors: Amporn Wiengmoon, Pattama Apichai, John T.H. Pearce, Torranin Chairuangsri
• Keywords: Age Hardening, Cast Al-Si-Cu Alloy, Mechanical Property, Microstructure

References

[1] S. Haro, J. Ramírez, D. K. Dwivedi, E. Martínez, Influence of solutionising and aging temperatures on microstructure and mechanical properties of cast Al-Si-Cu alloy, Mater. Sci. Technol. 25(7) (2009) 886-891.

DOI: 10.1179/174328408x327722

[2] H.Chandler, Heat treater's guide practices and procedures for nonferrous alloys, ASM International, Materials Park, OH, 1996.

[3] E. Rincon, H. F. Lopez, M. M. Cisneros, H. Mancha, Temperature effects on the tensile properties of cast and heat treated aluminium alloy A319, Mater. Sci. Eng. A. 519 (2009) 128-140.

DOI: 10.1016/j.msea.2009.05.022

[4] R. Mahmudi, P. Sepehrb, H. M. Ghasemi, Improved properties of A319 aluminum casting alloy modified with Zr, Mater. Lett. 60 (2006) 2606-2610.

DOI: 10.1016/j.matlet.2006.01.046

[5] S.P. Ringer, K. Hono, Microstructural evolution and age-hardening in aluminium alloys, Atom probe field-ion microscopy and transmission electron microscopy studies, Mater. Charact. 44 (2000) 101-131.

DOI: 10.1016/s1044-5803(99)00051-0

[6] R.E. Smallman, A.H.W. Ngan, Physical metallurgy and advanced materials, Elsevier, Butterworth-Heinemann, Oxford, 2007.

[7] D.O. Ovono, I. Guillot, D. Massinon, The microstructure and precipitation kinetics of a cast aluminium alloy, Scripta Mater. 55 (2006) 259-262.

DOI: 10.1016/j.scriptamat.2006.03.065

[8] A. Wiengmoon, J.T.H. Pearce, T. Chairuangsri, S. Isoda, H. Saito, H. Kurata, HRTEM and HAADF-STEM of precipitates at peak ageing of cast A319 aluminium alloy, Micron 45 (2013) 32-36.

DOI: 10.1016/j.micron.2012.10.009

[9] E. Rincon, H.F. L´opez, M. M. Cisneros, H. Mancha, M. A. Cisneros, Effect of temperature on the tensile properties of an as-cast aluminum alloy A319, Mater. Sci. Eng. A. 452–453 (2007) 682–687.

DOI: 10.1016/j.msea.2006.11.029