Crystallization Growth of Titanium Silicalite-1 over Monolithic Cordierite Support

Li Bin Yang; Zun Lu Zhu; Zuo Liang Sha

doi:10.4028/www.scientific.net/AMR.788.105

Paper Titles

Nonlinear Optical Properties of the AgGa_1-xIn_xSe₂ Crystal
p.85

Effects of Excess Bismuth Content on Microstructure and Electric Properties of Europium-Substituted Bismuth Titanate Thin Films
p.89

Effects of Electrode Size and Position on the Force-Frequency Characteristic of Integrated Resonator
p.95

Study on Transformation Behavior of Retained Austenite in TRIP Steel
p.100

Crystallization Growth of Titanium Silicalite-1 over Monolithic Cordierite Support
p.105

Effect of TiO₂ Nanoparticles on Cellulose Acetate Microporous Membrane Performance
p.110

Adsorption of In³⁺ from Aqueous Solutions by Persimmon Tannins-Immobilized Collagen Fiber
p.114

Study on Hydroxyapatite Fibers with Strontium Reinforced Calcium Phosphate Cement
p.119

Preparation and Characterization of Chelerythrine Nanoparticles Composed of Magnetic Multiwalled Carbon Nanotubes
p.127

HomeAdvanced Materials ResearchAdvanced Materials Research Vol. 788Crystallization Growth of Titanium Silicalite-1...

Crystallization Growth of Titanium Silicalite-1 over Monolithic Cordierite Support

Abstract:

Titanium silicalite-1(TS-1) membranes were prepared on cordierite support by hydrothermal treatment. The TS-1 membranes were characterized by scanning electron microscope (SEM), X-ray diffractometer (XRD) and FT-IR, The factor that the ratio of TPA+/Si on influencing TS-1 crystal was investigated and it was indicated that the ratio of TPA+/Si had a strong effect on its morphology. The TS-1 crystal presented ellipsoid when ratio of TPA+/Si was 0.15. However, the morphology of TS-1 crystal changed to coffin-shaped when the ratio of TPA+/Si increased to 0.4. Each lattice plane of TS-1 crystal grew on cordierite support with different speed which was controlled by concentration of structure-directing agent SDA (TPAOH) in precursor solution. The mechanism of TS-1 crystal growth on cordierite support maybe that the TPA+ in the solution attracts silicate species, titanium species to form inorganic-organic composite species, the aggregation the inorganic-organic composite species formed crystal nucleus, the morphologies changed due to the growth rate of different lattice planes.