Study on Properties of Modified Poplar Wood

Yong Wang; Ze Jun Chen; La Yun Deng; You Hua Fan

doi:10.4028/www.scientific.net/AMR.926-930.242

Paper Titles

Role of Nitrite Ions and Natural Organic Matters as Photosensitizers on Photolysis of Phenol
p.226

Solvent-Dependent Catalytic Behavior of Hydrophobic Guest Artificial Glutathione Peroxidase Determined Using H₂O₂ and 4-Nitrobenzenethiol as Substrates
p.230

Studies on the Geometric and Electronic Structures of SiC Polytypes
p.234

Study on Active Ingredient of Blueberry Pomace in Fermentation by Lentinus edodes Hypha
p.238

Study on Properties of Modified Poplar Wood
p.242

Study on Surfacing Technics of 18CrNiWA Engine Crankshaft Surfacing Welding with Flux-Cored Wire
p.246

Study on the Anti-Rust Mechanism of Compound Rust Inhibitor TW742
p.250

Study on the Synthesis Process of Carbon Nanotubes
p.254

Synthesis and Characteristics of Hierarchical Nanostructure Fe₃O₄ Coated Multi-Walled Carbon Nanotubes
p.258

HomeAdvanced Materials ResearchAdvanced Materials Research Vols. 926-930Study on Properties of Modified Poplar Wood

Study on Properties of Modified Poplar Wood

Abstract:

The paper based on a comparative study between poplar wood and modified poplar wood, concerning dimensional stability, physical and mechanical properties. The result showed that air-dry density and ASE value of modified wood samples were increasing in different levels with change of the modifier concentration, compared with untreated poplar wood. The air-dry density of modified wood reached 0.41 g/cm3 with increase of 5.3% compared to poplar wood. ASE reached 47.8% and the water-absorption ratio decreased by 38% at most when the modifier concentration was 30 wt.%. Moreover, the MOE and MOR of modified poplar wood increased up to 27.4% and 13% respectively when the modifier concentration was 25 wt.%. The SEM spectrum showed some wood rays and the gaps between staggered fibers were filled by modifier.