Influence of Carbon Cloth Filaments Upon the Properties of 2D C/SiC via Precursor Infiltration and Pyrolysis Process
In this paper, 2D C/SiC composites with different carbon cloth filaments (1K, 3K) were prepared via precursor infiltration and pyrolysis (PIP) process. The flexural strength of 2D-1K C/SiC composites was 380MPa, and fracture toughness was 16.8MPa-m1/2, while those of 2D-3K C/SiC were 305MPa and 14.4MPa-m1/2, respectively. The differences of these two composites were analyzed from fiber volume ratio in the composites, density, and fracture surface (SEM) of the samples.
Wei Pan and Jianghong Gong
F. Zhang et al., "Influence of Carbon Cloth Filaments Upon the Properties of 2D C/SiC via Precursor Infiltration and Pyrolysis Process", Key Engineering Materials, Vols. 368-372, pp. 1041-1043, 2008