Influence of the Crack Widening on the Transverse Cracking in Lamellar Metal-Ceramic Composites

Romana Piat; Maria Kashtalyan; Igor Guz

doi:10.4028/www.scientific.net/KEM.754.83

Paper Titles

The Strange Case of Compacted Graphite Iron: A Remarkable Option with Unique Material Properties or an Unusable Alloy?
p.67

Fracture Toughness Characterization of Carbon Bonded Alumina Using Chevron Notched Specimens
p.71

Experimental Study of Fatigue Crack Initiation and Strain Evolution around a Micro-Void by In Situ SEM and Digital Image Correlation
p.75

Experimental Characterization of Competition of Surface and Internal Damage in Very High Cycle Fatigue Regime
p.79

Influence of the Crack Widening on the Transverse Cracking in Lamellar Metal-Ceramic Composites
p.83

Buckling and Post-Buckling Behaviour of Impacted Glass Reinforced Composite Plates under Compression after Impact Tests
p.87

The Evaluation of Deformation and Fracture of Gilsocarbon Graphite Subject to Service Environments: Experimental and Modelling
p.91

Effect of Shrinkage Porosity and Degenerated Graphite on Fatigue Crack Initiation in Ductile Cast Iron
p.95

Fracture-Mechanics Behaviour of Ceramic Foam with Macroscopic Stress Concentrator upon the Tensile Test
p.99

HomeKey Engineering MaterialsKey Engineering Materials Vol. 754Influence of the Crack Widening on the Transverse...

Influence of the Crack Widening on the Transverse Cracking in Lamellar Metal-Ceramic Composites

Abstract:

Stress field in the ceramic layer containing multiple transverse cracks is determined using a modified 2-D shear lag approach and a finite element method.

You might also be interested in these eBooks

Advances in Fracture and Damage Mechanics XVI

View Preview

Info:

Periodical:

Key Engineering Materials (Volume 754)

Pages:

83-86

DOI:

https://doi.org/10.4028/www.scientific.net/KEM.754.83

Citation:

Cite this paper

Online since:

September 2017

Authors:

Romana Piat*, Maria Kashtalyan, Igor Guz

Keywords:

Analytical Modeling, Damage Modeling, Finite Element Modeling, Metal-Matrix Composites, Transverse Cracking

Export:

RIS, BibTeX

Price:

Permissions CCC:

Request Permissions

Permissions PLS:

Request Permissions

Сopyright:

Citation:

* - Corresponding Author

References

[1] T. Ziegler, A. Neubrand, R. Piat: Comp. Sci. and Tech., Vol. 70 (2010), p.664.

Google Scholar

[2] S. Roy et al.: Mater. Sci. & Eng. A, Vol. 528 (2011), p.8226.

Google Scholar

[3] Y. Sinchuk et. al.: Mater. Sci. & Eng. A, Vol. 585 (2013), p.10.

Google Scholar

[4] M. Kashtalyan, Y. Sinchuk, R. Piat, I. Guz: Arch Appl Mech Vol. 86 (2016), p.177.

Google Scholar

[5] M. Kashtalyan, R. Piat, I. Guz: Procedia Structural Integrity Vol. 2 (20016), p.3377.

Google Scholar