Study on Preparation of PA6 / PDMS Blended Fibers and Fabric Properties

Abstract:

PA6 fibers and fabric properties were studied by adding PDMS, and PA6 / PDMS blend fibers were prepared by melt spinning. The experiment found that the addition of PDMS can significantly promote the rheology of the PET / PDMS blend melt. DSC tests show that the addition of PDMS has basically no effect on its crystallization and melting characteristics. With the increase of PDMS content, the contact angle of water on the blended fabric surface increased. KES-FB was used to evaluate fabrics made from PA6 / PDMS blended fibers. It was found that with the increase of PDMS content, the softness and elasticity of the fabrics were improved, and the stain resistance experiments showed that the modified fabrics had good resistance dirty performance.

• Periodical: Materials Science Forum (Volume 1003)
• Pages: 219-227
• DOI: https://doi.org/10.4028/www.scientific.net/MSF.1003.219
• Online since: July 2020
• Authors: Dong Sun, Guang Li*
• Keywords: Fabric Properties, Polyamide, Polydimethylsiloxane, Rheology

References

[1] D.R. Wu, Y.B. Sun, H. Liu, et al. Melt spinning properties of nylon 6 / NYC blends [J]. Chinese Journal of Colloid & Polymer, 2008, 26 (2): 22-24.

[2] T. T. Zhang, X. F. Zhao, Study on modification of nylon 6 [J]. Shanxi Chemical Industry, 2018, 38 (04): 132-134.

[3] L.Q. Zhang, Z.J. Li, Development status of polyester, nylon and polypropylene industrial yarn markets at home and abroad (1) [J]. Technical Textiles, 2007 (08): 1-6 + 14.

[4] M. Chang, Analysis and Prospect of China's Nylon 6 Chips Market [J]. Economic Analysis of China Petroleum and Chemical Industry, 2019 (07): 58-60.

[5] T.B.Q. Shen, D.C. Wu , X.G. Xie, Rheology and morphology of nylon-6 blends and blended fillers [J]. Plastics, 1991 (03): 13-16.

[6] W. Xi, Application and development of organosilicon compounds in fabric finishing [J] .Fine Chemical Information, 1988 (12): 1-9.

[7] D.F. Da Silva, D.C. Bezerra, L.T.A. Reul, et al. Rheological Study of Polyamide 6/Waste Styrene-Butadiene Rubber (SBR) Blends[C]// Materials Science Forum. (2012).

DOI: 10.4028/www.scientific.net/msf.727-728.1908

[8] J.F. Huang, J.F. Ge, W.J. Liang, F.A. Zhang, Rheological properties of polydimethylsiloxane / phenyl MDQ silicone resin hybrid system [J]. Polymer Materials Science and Engineering, 2015, 31 (02): 103 -107. He Sanxiong, Wu Wei, Wang Ru. Preparation and Properties of PA6 / SEBS-g-MAH / OMMT / GMA Blends [J]. Plastic Industry, 2011, 39 (04): 78-81.

[9] J.G. Zhang, J. Deng ,The Effect of Maleic Anhydride Grafted Styrene-Ethylene-Butylene-Styrene on the Friction and Wear Properties of Polyamide6/Carbon Nanotube Composites[J]. Polymer-Plastics Technology and Engineering, 2011, 50(15):1533-1536.

DOI: 10.1080/03602559.2011.603778

[10] X.D. Tang, Research progress of silicon-containing polymer antifouling coatings [J]. Modern Chemical Industry, 2007 (S2): 100-102.

[11] H.G. Wang, T.T. Li, Y.X. Jiang, H.D. Xie, Study on the Preparation of Silicone Fluorine Finishing Agent and Its Water-Repellent and Soil-Repellent Performance of Worsted Wool Fabrics [J]. Wool Spinning Technology, 2013, 41 (06): 39-42.

[12] S.X. He, W. Wu, R. Wang, Preparation and Properties of PA6 / SEBS-g-MAH / OMMT / GMA Blends [J]. China Plastics Industry, 2011, 39 (04): 78-81.

[13] J.P. Zhou, S. Chen, Analysis and application of KES fabric style meter test index [J]. Advanced Textile Technology, 2005 (06): 41-44.

[14] Z.Y. Zou, The principle and application of fabric style instrument [J] .Jiangsu Silk, 1989 (06): 20-28.

[15] H.Y. Yang, Study on the contact pressure comfort of different fiber fabrics [D]. Donghua University, (2014).

[16] Y.B. Wei, Q.F. An, J. Zhao, Application status and development of silicone softener in fabric finishing [J]. Silicone Materials, 2014, 28 (06): 479-483.