Severe Plastic Deformation of Copper, Binary Cu-Zn Solid-Solution Alloys, and High-Strength Brass by High-Pressure Torsion

Article Preview

Abstract:

Severely-deformed high-strength brasses were investigated by leveraging high-pressure torsion (HPT) processing in order to obtain more enhanced mechanical properties of copper alloys. Pure copper, binary Cu-Zn solid-solution alloys and high-strength brasses including aluminum and manganese additions were selected for experiments. For comparison of these materials, zinc equivalent parameter was used. These materials were subjected to the HPT processing, followed by hardness tests and tensile tests. The maximal hardness value of the nanostructured high-strength brass with β phase matrix was reached 420 HV. The HPT processed high-strength brass with β phase matrix showed significant increase in the yield stress and tensile strength with sacrificing ductility. The tensile specimen of the high-strength brass with β phase matrix was fractured before initiation of necking. It was found that utilizing β phase matrix is also beneficial for controlling enhanced strength of high-strength copper alloys for not only casting process but also severe plastic deformation.

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volume 1016)

Pages:

780-785

Citation:

Online since:

January 2021

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2021 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

* - Corresponding Author

[1] T. Kunimine, N. Takata, N. Tsuji, T. Fujii, M. Kato, S. Onaka, Temperature and strain rate dependence of flow stress in severely deformed copper by accumulative roll bonding, Mater. Trans. 50 (2009) 64-69.

DOI: 10.2320/matertrans.md200809

Google Scholar

[2] T. Kunimine, T. Fujii, S. Onaka, N. Tsuji, M. Kato, Effects of Si addition on mechanical properties of copper severely deformed by accumulative roll-bonding, J. Mater. Sci. 46 (2011) 4290-4295.

DOI: 10.1007/s10853-010-5235-4

Google Scholar

[3] T. Kunimine, T. Aragaki, T. Fujii, S. Onaka, M. Kato, Inverse temperature dependence of activation volume in ultrafine-grained copper processed by accumulative roll-bonding, J. Mater. Sci. 46 (2011) 4302-4307.

DOI: 10.1007/s10853-010-5243-4

Google Scholar

[4] H. Watanabe, T. Kunimine, C. Watanabe, R. Monzen, Y. Todaka, Tensile deformation characteristics of a Cu−Ni−Si alloy containing trace elements processed by high-pressure torsion with subsequent aging, Mater. Sci. Eng. A 730 (2018) 10-15.

DOI: 10.1016/j.msea.2018.05.090

Google Scholar

[5] T. Kunimine, M. Watanabe, A comparative study of hardness in nanostructured Cu−Zn, Cu−Si and Cu−Ni solid-solution alloys processed by severe plastic deformation, Mater. Trans. 60 (2019) 1484-1488.

DOI: 10.2320/matertrans.mf201944

Google Scholar

[6] P.C.J. Gallagher, The influence of alloying, temperature, and related effects on the stacking fault energy, Metall. Trans. 1 (1970) 2429-2461.

DOI: 10.1007/bf03038370

Google Scholar

[7] C. Yang, Z. Ding, Q.C. Tao, L. Liang, Y.F. Ding, W.W. Zhang, Q.L. Zhu, High-strength and free cutting silicon brasses designed via the zinc equivalent rule, Mater. Sci. Eng. A 723 (2018) 296-305.

DOI: 10.1016/j.msea.2018.03.055

Google Scholar

[8] J. Dutkiewicz, F. Masdeu, P. Malczewski, A. Kukuła, Microstructure and properties of α + β brass after ECAP processing, Arch. Mater. Sci. Eng. 39 (2009) 80-83.

Google Scholar

[9] K. Edalati, Z. Horita, A review on high-pressure torsion (HPT) from 1935 to 1988, Mater. Sci. Eng. A 652 (2016) 325-352.

DOI: 10.1016/j.msea.2015.11.074

Google Scholar

[10] Non-ferrous materials, The Japan Institute of Metals and Materials, Sendai, (1987).

Google Scholar

[11] X.X. Wu, X.Y. San, Y.L. Gong, L.P. Chen, C.J. Li, X.K. Zhu, Studies on strength and ductility of Cu-Zn alloys by stress relaxation, Mater. Des. 47 (2013) 295-299.

DOI: 10.1016/j.matdes.2012.12.020

Google Scholar

[12] Q. Wei, S. Cheng, K.T. Ramesh, E. Ma, Effect of nanocrystalline and ultrafine grain sizes on the strain rate sensitivity and activation volume: fcc versus bcc metals, Mater. Sci. Eng. A 381 (2004) 71-79.

DOI: 10.1016/j.msea.2004.03.064

Google Scholar