Formation of Nanocale Oxide Particles and Evaluation of Threshold Stress of Fe-9Cr-0.2Ti-0.3Y2O3 Nanostructured Ferritic Alloy

Article Preview

Abstract:

Nanostructured ferritic alloys (NFA) of Fe-9Cr-0.2Ti-0.3Y2O3 (in mass) incorporating nanoscale oxide particles, was produced by mechanical milling (MM) followed by hot pressing (HP). The formation process of the nanoscale oxide particles were structurally characterized at each step of the elaboration processes by means of transmission electron microscope (TEM). The observations of structure of the mixed powders and the nanoscale oxide particles in the NFA after MM indicated that the initial powders, coupled with the original yttria powders, get fractured by severe plastic deformation and ultrafine bcc grains (~20 nm) of the matrix, and Y2O3 nanocrystals with irregular edges are formed during MM. The addition of titanium (Ti) promotes the formation of amorphous phase of [YMamorphous during MM. Microstructure of the NFA observed by TEM exhibited a very fine structure of nanostructured grains in which large number of nanoscale oxide particles were distributed after HP process. HRTEM observations of partially and fully crystallized oxide nanoparticles in the matrix of NFA gain an insight into the formation mechanism of nanoscale oxide particles in HP process. The formation process of nanoscale oxide particles consist of the reaction between Y2O3 fragments and titanium (Ti) and crystallization of [YMamorphous.Threshold stress which can quantitatively shows the effect of dispersion strengthening was carefully evaluated on the basis of higher magnified images of the nanoscale oxide particles. Different values of threshold stress were obtained due to the various dispersions of the nanoscale oxide particles within different areas. That may be the reason why the threshold stress cannot be clearly obtained by the results of creep tests.

You might also be interested in these eBooks

Info:

Periodical:

Materials Science Forum (Volumes 745-746)

Pages:

398-406

Citation:

Online since:

February 2013

Export:

Price:

Permissions CCC:

Permissions PLS:

Сopyright:

© 2013 Trans Tech Publications Ltd. All Rights Reserved

Share:

Citation:

[1] S. J. Zinkle, Fusion materials science: overview of challenges and recent progress, Phys. Plasmas, 2005, 12: 058101.

DOI: 10.1063/1.1880013

Google Scholar

[2] J. Ribis, M. L. Lescoat, Y. de Carlan, J. M. Costantini, I. Monnet , T. Cozzika, F. Delabrouille, J. Malaplate, Stability of nano-oxides upon heavy ion irradiation of an ODS material, J. Nucl. Mater, 2011, 417: 262~265.

DOI: 10.1016/j.jnucmat.2010.12.068

Google Scholar

[3] M. C. Brandes, L. Kovarik, M. K. Miller, G. S. Daehn, M. J. Mills, Creep behavior and deformation mechanisms in a nanocluster strengthened ferritic steel, Acta Mater, 2012, 60: 1827~1839.

DOI: 10.1016/j.actamat.2011.11.057

Google Scholar

[4] S. Ohtsuka, S. Ukai, M. Fujiwara, T. Kaito, T. Narita, Nano-structure control in ODS martensitic steels by means of selecting titanium and oxygen contents, J. Phys. Chem. Solids, 2005, 66: 571–575.

DOI: 10.1016/j.jpcs.2004.06.033

Google Scholar

[5] C. Z. Yu, H. Oka, N. Hashimoto, S. Ohnuki, Development of damage structure in 16Cr–4Al ODS steels during electron-irradiation 2011, doi: 10. 1016/j. jnucmat. 2011. 02. 037.

DOI: 10.1016/j.jnucmat.2011.02.037

Google Scholar

[6] P. Unifantowicza, R. Schäublina, C. Hébertb, T. Płocińskic, G. Lucasb, N. Baluca, Statistical analysis of oxides particles in ODS ferriticsteel using advanced electron microscopy, J. Nucl. Mater, 2012, 422: 131~136.

Google Scholar

[7] F. Corpace, A. Monnier, A. P. Quintin, J. P. Manaud, Phenomena leading to a modification of the nano-sized structure during resistance upset welding of ODS steel cladding, Mater. Sci. Forum, 2012, 706~709: 977~982.

DOI: 10.4028/www.scientific.net/msf.706-709.977

Google Scholar

[8] L. Zhang, S. Ukai, T. Hoshino, S. Hayashi, X. Qu, Y2O3 evolution and dispersion refinement in Co-base ODS alloys, Acta Mater, 2009, 57: 3671~3682.

DOI: 10.1016/j.actamat.2009.04.033

Google Scholar

[9] S. Ukai, S. Mizuta, M. Fujiwara, T. Okuda, T. Kobayashi, Development of 9Cr-ODS martensitic steel claddings for fuel pins by means of ferrite to austenite phase transformation, J. Nucl. Sci. Technol, 2002, 39: 778–788.

DOI: 10.1080/18811248.2002.9715260

Google Scholar

[10] L. L. Hsiung, M. J. Fluss, S. J. Tumey, B. W. Choi, Y. Serruys, F. Willaime, A. Kimura, Formation mechanism and the role of nanoparticles in Fe-Cr ODS steels developed for radiation tolerance, Phys. Rev. B, 2010, 82: 184103.

DOI: 10.1103/physrevb.82.184103

Google Scholar

[11] T. Koyano, T. Takizawa, T. Fukunaga, U. Mizutani, Mechanical alloying process of Fe-Cr powders studied by magnetic measurements, J. Appl. Phys, 1993, 73: 429~433.

DOI: 10.1063/1.353867

Google Scholar

[12] C. Suryanarayana, E. Ivanov, V. V. Boldyrev, The science and technology of mechanical alloying. Mater. Sci. Eng. A, 2001, 304~306: 151~158.

DOI: 10.1016/s0921-5093(00)01465-9

Google Scholar

[13] S. Ukai, T. Okuda, M. Fujiwara, T. Kobayashi, S. Mizuta, H. Nakashima, Characterization of high temperature creep properties in recrystallized 12Cr–ODS ferritic steel claddings, J. Nucl. Sci. Technol, 2002, 39: 872~879.

DOI: 10.1080/18811248.2002.9715271

Google Scholar

[14] H. Sakasegawa, L. Chaffron, F. Legendre, M. Brocq, L. Boulanger, S. Poissonnet, Y. de Carlan,J. Bechade, T. Cozzika, J. Malaplate, Evaluation of threshold stress of the MA957 ODS ferrtic alloy, J. Nucl. Mater, 2009, 386~388: 511~514.

DOI: 10.1016/j.jnucmat.2008.12.151

Google Scholar

[15] L. Dai, Y. C. Liu, Z. Q. Ma, Z. Z. Dong, L. M. Yu, Microstructural evolution of oxide-dispersion-strengthened Fe–Cr model steels during mechanical milling and subsequent hot pressing, J. Mater. Sci, 2012, doi: 10. 1007/s10853-012-6948-3.

DOI: 10.1007/s10853-012-6948-3

Google Scholar